Effect of Vanadium on Microstructure and Corrosion Resistance of 2205 Duplex Stainless Steel

Xiu Sun1,2*, Zhongmin Yang2, Ying Chen2, Jianwen Hu1, Xiaobin Li3, Shanglin Lv3

1Hebei University of Science and Technology, Shijiazhuang Hebei

2Deparment for Structure Steel, Central Iron and Steel Research Institute, Beijing

3Central Research Institute of Building and Construction of MCC Group, Beijing

Received: Jul. 22nd, 2018; accepted: Aug. 13th, 2018; published: Aug. 20th, 2018

ABSTRACT

The microstructure and electrochemical corrosion resistance of V microalloyed 2205 duplex stainless steels and 2205 duplex stainless steels without V were investigated at 900˚C and 950˚C for solution treatment and holding time respectively. The results show that the 2205 stainless steel reinforcement containing V was solution treated at 950˚C. The brittleness of the structure was significantly reduced compared with that of 2205 stainless steel without V. In the temperature range of 1000˚C~1050˚C, there is no σ brittle phase in the two kinds of 2205 stainless steel bars. The addition of microalloying V inhibited the brittle phase precipitation. The critical pitting point of 2205 stainless steel with V is higher than the critical pitting point of 2205 stainless steel without V, which improves the corrosion resistance of 2205 duplex stainless steel.

Keywords:Microalloying Element V, 2205 Duplex Stainless Steel, Critical Pitting Point

V对2205双相不锈钢钢筋组织和耐蚀性能影响研究

孙秀1,2*,杨忠民2,陈颖2,胡建文1,李晓滨3,吕尚霖3

1河北科技大学材料学院,河北 石家庄

2钢铁研究总院工程用钢研究所,北京

3中冶建筑研究总院有限公司,北京

收稿日期:2018年7月22日;录用日期:2018年8月13日;发布日期:2018年8月20日

摘 要

本文对比了V微合金化2205双相不锈钢钢筋和不含V的2205双相不锈钢钢筋经过不同固溶处理的组织和电化学腐蚀性能,结果表明:含V的2205不锈钢钢筋在950℃固溶处理时组织中的脆性相比不含V的2205不锈钢钢筋组织中的脆性相显著减少,在1000℃~1050℃温度区间内,含V的2205钢筋和不含V的2205钢筋的微观组织中都没有σ相等脆性相析出,添加V有抑制脆性相析出的作用。含V的2205不锈钢钢筋的临界点蚀电位高于不含V的2205不锈钢钢筋的临界点蚀电位,添加V提高了2205双相不锈钢的耐腐蚀性能。

关键词 :微合金元素V2205,双相不锈钢,临界点蚀电位

Copyright © 2018 by authors and Hans Publishers Inc.

This work is licensed under the Creative Commons Attribution International License (CC BY).

http://creativecommons.org/licenses/by/4.0/

1. 引言

2205双相不锈钢集良好的力学性能、优良的耐应力腐蚀开裂性能、可焊接性和相对的经济性于一体,使得其广泛应用于油气、石化、桥梁、建筑等领域 [1] [2] [3] 。然而,2205双相不锈钢钢筋的研究报道很少,特别是在2205双相不锈钢中添加微合金元素轧制螺纹钢筋的文章还未见报道。本文重点以含V和不含V的2205双相不锈钢钢筋为研究对象,研究了不同固溶温度、保温时间对组织特征的影响和耐腐蚀性能的影响。

2. 实验方法

2205双相不锈钢钢筋的化学成分见表1。含V的钢筋来自江阴市西城钢铁有限公司,不含V的钢筋来自攀钢集团长城特殊钢有限公司。试样从热轧态2205双相不锈钢钢筋上横向截取。在实验室热处理炉中进行固溶处理,固溶处理温度为950℃、1000℃和1050℃,保温时间分别为1 h、2 h、3 h。试样进行金相样品制备,经过机械磨抛、电解腐蚀后采用光学显微镜(OM)场发射扫描电镜(SEM)对试样进行组织观察。采用273A电化学工作站对试样进行点蚀电位测试。

3. 实验结果及分析

3.1. 不同固溶处理制度的2205双相不锈钢钢筋的SEM观察

用10% KOH水溶液,电压6~10 V,电解腐蚀1 min。样品腐蚀后,在金相显微镜下观察,500倍放大倍数。含V2205双相不锈钢钢筋在950℃、1000℃和1050℃固溶不同时间下的组织特征如图1所示,不含V2205双相不锈钢钢筋的组织特征如图2所示。

(a) (b) (c) (d) (e) (f) (g) (h) (i)

Figure 1. The microstructure of different time at solution temperature of 950˚C with V. (a) The solid solution temperature: 950˚C, heat preservation 1 h; (b) The solid solution temperature: 950˚C, heat preservation 2 h; (c) The solid solution temperature: 950˚C, heat preservation 3 h; (d) The solid solution temperature: 1000˚C, heat preservation 1 h; (e) The solid solution temperature: 1000˚C, heat preservation 2 h; (f) The solid solution temperature: 1000˚C, heat preservation 3 h; (g) The solid solution temperature: 1050˚C, heat preservation 1 h; (h) The solid solution temperature: 1050˚C, heat preservation 2 h; (i) The solid solution temperature: 1050˚C, heat preservation 3 h

图1. 含V固溶温度950℃不同保温时间的组织特征。(a) 固溶温度:950℃,保温1 h;(b) 固溶温度:950℃,保温2 h;(c) 固溶温度:950℃,保温3 h;(d) 固溶温度:1000℃,保温1 h;(e) 固溶温度:1000℃,保温2 h;(f) 固溶温度:1000℃,保温3 h;(g) 固溶温度:1050℃,保温1 h;(h) 固溶温度:1050℃,保温1 h;(i) 固溶温度:1050℃,保温3 h

(a) (b) (c) (d) (e) (f) (g) (h) (i)

Figure 2. The microstructure of different time at solution temperature of 950˚C without V. (a) The solid solution temperature: 950˚C, heat preservation 1 h; (b) The solid solution temperature: 950˚C, heat preservation 2 h; (c) The solid solution temperature: 950˚C, heat preservation 3 h; (d) The solid solution temperature: 1000˚C, heat preservation 1 h; (e) The solid solution temperature: 1000˚C, heat preservation 2 h; (f) The solid solution temperature: 1000˚C, heat preservation 3 h; (g) The solid solution temperature: 1050˚C, heat preservation 1 h; (h) The solid solution temperature: 1050˚C, heat preservation 2 h; (i) The solid solution temperature: 1050˚C, heat preservation 3 h

图2. 不含V固溶温度950℃ 不同保温时间的组织特征。(a) 固溶温度:950℃,保温1 h;(b) 固溶温度:950℃,保温2 h;(c) 固溶温度:950℃,保温3 h;(d) 固溶温度:1000℃,保温1 h;(e) 固溶温度:1000℃,保温2 h;(f) 固溶温度:1000℃,保温3 h;(g) 固溶温度:1050℃,保温1 h;(h) 固溶温度:1050℃,保温1 h;(i) 固溶温度:1050℃,保温3 h

Table 1. Chemical composition of the tested steels (wt%)

表1. 2205双相不锈钢钢筋主要化学成分(wt%)

对比含V的2205钢筋和不含V的2205钢筋经过不同固溶处理后的组织,可以看出,在950℃固溶处理,组织中有不同于奥氏体和铁素体相的其他相析出,且随着保温时间的延长,析出相数量增加 [4] [5] 。950℃下含V的2205钢筋的组织中奥氏体和铁素体相界处脆性相析出量比不含V的少很多,说明含V的微合金化2205不锈钢由于V的存在降低了自由能,抑制了脆性相的析出。在1000℃~1050℃温度区间内,含V的2205钢筋和不含V的2205钢筋的微观组织中都没有σ相等脆性相析出,只有深色的α相和浅色的γ相。随着保温时间延长,组织有长大的趋势。采用金相显微镜附带的Pro-imaging图像分析仪软件按照GB/T6401-1986标准测量并计算相比例(按灰度区分深浅颜色面积之比)。为获得更加准确的结果,每个试样在500倍下测量10个视场,计算相比例的平均值。其在不同固溶温度和保温时间下的相的具体含量见图3。当固溶温度为950℃时,脆性相比例随着保温时间延长而增加,铁素体含量减少,原因是随保温时间的延长,铁素体中发生了共析反应α → γ2 + σ,σ相在界面处不断形核并向铁素体相内长大,使得其含量不断增加,铁素体含量不断减少。在1000℃~1050℃温度区间内,无σ相等脆性相析出,α相:γ相的比例接近为1:1。

3.2. 含V和不含V的2205不锈钢钢筋950℃固溶处理的SEM观察

分别选取含V和不含V的2205不锈钢钢筋在950℃保温3小时的固溶处理金相样品进行SEM观察,结果如图4图5所示。950℃固溶处理的SEM观察到奥氏体和铁素体相界存在块状析出物,能谱扫描发现析出相中含有Fe、Cr、Mo、Ca、O等元素。推测析出物优先在相界面的夹杂物复合析出。

3.3. 含V的2205不锈钢钢筋和不含V的2205不锈钢钢筋的电化学腐蚀试验

分别选取含V和不含V的2205不锈钢钢筋固溶处理样品进行点蚀电位测试,根据GBT 17899-1999标准在3.5%的NaCl溶液中测得的点蚀电位如表2所示。实验装置采用经典的三电极体系(如图6),将固溶处理完的两种2205不锈钢钢筋用线切割机切为尺寸为10 × 10 × 2.5 mm的样品,并且每一组准备3个平行试样。先将方形试样去除氧化皮和油脂,然后用在其一端焊上导线,用环氧树脂封样,放入真空箱静置72 h,固化后,打磨、抛光以备测量。从图7可以看出:含V的2205不锈钢钢筋的点蚀电位高于不含V的点蚀电位,说明含V的2205不锈钢钢筋由于V的存在,减弱了脆性相析出,提高了耐腐蚀性能 [6] [7] [8] [9] 。

4. 结论

1) 含V的2205不锈钢钢筋在950℃固溶处理,组织中的脆性相比不含V的2205不锈钢钢筋组织中的脆性相显著减少。说明添加微合金元素V有抑制脆性相析出的作用。在1000℃~1050℃温度区间内,无σ相等脆性相析出,α相:γ相的比例接近为1:1。

2) 含V的2205不锈钢钢筋的临界点蚀电位高于不含V的2205不锈钢钢筋的临界点蚀电位。说明添加微合金元素提高了2205双相不锈钢的耐腐蚀性能。

3) 添加微合金元素抑制脆性相析出,将有利于降低固溶处理温度,对节能降耗发挥积极作用。

(a) (b)

Figure 3. Phase proportion at different solution treatment. (a) Vanadium; (b) Do not contain vanadium

图3. 不同固溶温度下和保温时间下的相含量。(a) 含钒;(b) 不含钒

(a)(b)

Figure 4. The images of 950˚C solution treatment with V for 3 hour. (a) Morphology; (b) Energy spectrum

图4. 含V950℃固溶保温3小时的扫描照片。(a) 形貌;(b) 能谱

(a) (b) (c)

Figure 5. The images of 950˚C solution treatment without V for 3 hour. (a) Morphology; (b), (c) Energy spectrum

图5. 不含V950℃固溶保温3小时的扫描照片。(a) 形貌;(b)、(c) 能谱

Figure 6. Standard three electrode cell of electrochemical test

图6. 电化学三电极体系

Figure 7. Critical pitting point of 2205 duplex stainless steel under different solution treatment

图7. 不同固溶处理条件下2205双相不锈钢点蚀电位

Table 2. Critical pitting point of 2205 duplex stainless steel under different solution treatment

表2. 不同固溶处理条件下2205双相不锈钢的临界点蚀电位

基金项目

国家高技术研究发展计划(863计划)资助项目(2015AA03A502)。

文章引用

孙 秀,杨忠民,陈 颖,胡建文,李晓滨,吕尚霖. V对2205双相不锈钢钢筋组织和耐蚀性能影响研究
Effect of Vanadium on Microstructure and Corrosion Resistance of 2205 Duplex Stainless Steel[J]. 冶金工程, 2018, 05(03): 122-130. https://doi.org/10.12677/MEng.2018.53017

参考文献

  1. 1. 武英杰, 申鹏, 颜海涛. 双相不锈钢的国内外研究进展[J]. 科技创新导报, 2010(28): 41.

  2. 2. Olsson, L. (1994) 60 Years of Duplex Stainless Steel Applications. National Association of Corrosion Engineers International Annual Con-ference, Baltimore, 28 February-4 March 1994.

  3. 3. 王刚, 郭幼丹, 郭雷, 等. 双相不锈钢的发展特点及其应用[J]. 科技与创新, 2015(7): 91-92.

  4. 4. 刘复兴. S32205双相不锈钢中σ相的析出及其对力学性能的影响[J]. 钢铁, 2010, 45(7): 62-65 + 93.

  5. 5. 刘雄, 何燕霖, 丁秀平, 等. 高温时效对2205双相不锈钢中σ相析出行为的影响[J]. 材料热处理学报, 2010, 31(3): 48-51.

  6. 6. Angelini, E. and De Benedetti, B. (2004) Microstructural Evolution And-localized Corrosion Resistance of an Aged Super Duplex Stainless Steel. Corrosion Science, 46, 1351-1367. https://doi.org/10.1016/j.corsci.2003.09.024

  7. 7. 肖纪美. 不锈钢的金属学问题[M]. 北京: 冶金工业出版社, 2006.

  8. 8. 杨才福, 王瑞珍, 陈雪慧, 译. 钒在微合金钢中的作用[M]. 北京: 冶金工业出版社, 2015.

  9. 9. Ras, M.H. and Pistorius, P.C. (2002) Possible Mechanisms for the Improvement by Vanadium of the Pitting Corrosion Re-sistance of 18% Chromium Ferritic Stainless Steel. Corrosion Science, 44, 2479-2490. https://doi.org/10.1016/S0010-938X(02)00050-1

  10. NOTES

    *通讯作者。

期刊菜单