文章对老鸦巢铅锌矿床的黄铁矿和闪锌矿进行了矿相学及电子探针分析,认为黄铁矿和闪锌矿主要以自形–半自形粒状分布,黄铁矿粒径0.5~3 mm,晶形多呈五角十二面体,少量为立方体、球状、草莓状、胶状;闪锌矿粒径0.5~1 mm,从早到晚其颜色逐渐变浅,自形程度变差,晚期闪锌矿沿裂隙、空洞充填,呈葡萄状的集合体与八面体方铅矿共生;区内黄铁矿弱亏硫不亏铁,Co/Ni变化大,平均值大于1,As含量较高,显示具有中低温热液成因特征;闪锌矿富硫亏锌,且w(Mn) < 0.15%、w(Fe) < 6%、Ga/In < 1、Zn/Cd在114~140之间,Cd与Zn/Cd呈明显负相关性,同时FeS分子投图对应温度为170˚C~220˚C,指示闪锌矿中低温岩浆热液成因的特征。 Objective: Through petrography and electron probe analysis on pyrite and sphalerite in Laoyachao Pb-Zn deposit, it can be known from the mineral microscopy observation that it is concluded that the pyrite and sphalerite in this area is mainly euhedral or Hypautomorphic granular distribution, pyrite particle size of 0.5 - 3 mm, crystal shape is pentagonal dodecahedron, with a small amount being cube, spherical, strawberry and gelatinous. Sphalerite particle size is of 0.5 - 1 mm, from early to late its color gradually becomes shallow, and the degree of self-shape becomes worse. The late sphalerite is filled with fissures and cavities, and the grape-like sphalerite aggregates are symbiosis with octahedral galena. The pyrite is slightly depleted with S in this area, the Co/Ni changes greatly, the average value is more than 1, and the content of As is higher, which shows the characteristics of medium and low temperature hydrothermal genesis. The sphalerite is rich Sulphur and loss of zinc, and w(Mn) < 0.15%, w(Fe) < 6%, Ga/In < 1, Zn/Cd between 114 and 140, Cd and Zn/Cd are negatively correlated. And the corresponding temperature of FeS molecule is 170˚C - 220˚C, which indicates the origin of low temperature magmatic hydrothermal in sphalerite.
冯玉龙1,2,邵拥军1,2*,蒋梦同1,2,冯雨周1,2,宋泽友3
1中南大学有色金属成矿预测与地质环境监测教育部重点实验室,湖南 长沙
2中南大学地球科学与信息物理学院,湖南 长沙
3湖南省地质科学院,湖南 长沙
收稿日期:2017年7月30日;录用日期:2017年8月13日;发布日期:2017年8月21日
文章对老鸦巢铅锌矿床的黄铁矿和闪锌矿进行了矿相学及电子探针分析,认为黄铁矿和闪锌矿主要以自形–半自形粒状分布,黄铁矿粒径0.5~3 mm,晶形多呈五角十二面体,少量为立方体、球状、草莓状、胶状;闪锌矿粒径0.5~1 mm,从早到晚其颜色逐渐变浅,自形程度变差,晚期闪锌矿沿裂隙、空洞充填,呈葡萄状的集合体与八面体方铅矿共生;区内黄铁矿弱亏硫不亏铁,Co/Ni变化大,平均值大于1,As含量较高,显示具有中低温热液成因特征;闪锌矿富硫亏锌,且w(Mn) < 0.15%、w(Fe) < 6%、Ga/In < 1、Zn/Cd在114~140之间,Cd与Zn/Cd呈明显负相关性,同时FeS分子投图对应温度为170˚C~220˚C,指示闪锌矿中低温岩浆热液成因的特征。
关键词 :黄铁矿,闪锌矿,电子探针,老鸦巢铅锌矿床
Copyright © 2017 by authors and Hans Publishers Inc.
This work is licensed under the Creative Commons Attribution International License (CC BY).
http://creativecommons.org/licenses/by/4.0/
湖南省常宁市松柏镇水口山铅锌多金属矿田已经有上百年的开发历史,以铅锌为主要矿产产出,其次是铜、金、银等,被誉为“世界铅都”,而区域内老鸦巢Pb-Zn矿床位于矿田中部,是矿田内铅锌矿床的典型代表。水口山铅锌矿田从发现开始,就吸引了大批学者的关注,目前前人对于矿田的成矿地质特征 [
水口山矿田位于华夏古板块西北缘和扬子古板块东南缘交界处的钦杭成矿结合带中部,邵阳–郴州北西向深断裂带北侧、株洲–衡阳–宁远大断层东侧、耒阳–临武南北褶皱带北部(图1),是一个大型多金属矿田,矿田以产出多种金属矿产为特征,包括康家湾铅锌金矿、龙王山金矿以及水口山铅锌金多金属矿等。矿田内地层归属于湘南地层,出露地层自上泥盆统至新生界,其中上泥盆世晚期到三叠世早期,
(a) 1. 研究区;2. 古板块结合带(断线为推测部分);3. 断层及构造分区界线;4. 过渡性构造带界线;(b) 1. 白垩系–第三系;2. 元古代基底;3. 燕山期花岗岩;4. 新元古代–震旦系大洋型岩石圈俯冲带;5. 壳断层;6. 泥盆系–三叠系;7. 加里东花岗岩;8. 花岗闪长岩;9. 背斜轴;10. B型俯冲带;11. 震旦系–志留系;12. 印支期花岗岩;13. 玄武岩;14. 转换断层。
不间断连续沉积上千米的浅海相碳酸盐岩夹滨海相含煤砂页岩,晚三叠–白垩纪出露地层主要为陆源碎屑磨拉石建造。在石炭系壶天群(C2+3)的白云质灰岩内发现规模不大的高品位铜铅锌矿脉,大量的铅锌金银矿赋存于100米厚的二叠系下统栖霞组(Plq)灰岩中,而二叠系上统斗岭组(P2dl) 300多米厚的炭质页岩、夹煤层的粉砂岩,是矿田成矿主要的屏蔽层。
在中生代,由于印支运动造成了中国大陆发生大规模的碰撞和拼合,使得矿田在东西向区域应力挤压作用下,形成了一系列大小不一的南北向褶皱与不同方向的断裂。矿田内断裂构造主要为南北向展布,其次为北东至北北东向展布,为区域岩浆的侵入活动提供了通道。燕山运动继承发展了印支构造,使早期沉积并固结的白垩系红层产状发生改变,倒转偏向东,与此同时褶皱的逐渐倒转,致使大规模的叠瓦式双层结构推覆断层形成。这类断层与成岩、成矿和矿田中众多的金矿体有着密切的关系。
矿田内主要出露燕山期岩浆,具有壳、幔混源的特征,为I型岩浆岩,多数沿断裂构造侵入,定位于区域内的倒转背斜的核部和推覆构造带等部位,岩性为钙碱系列英安岩类中酸性岩石,出露区常见花岗闪长斑岩、花岗闪长岩、英安流纹斑岩、花岗斑岩等。而花岗闪长岩的浅成侵入系列多沿倒转背斜轴部侵入,与矿田早期铅锌铜硫金矿床关系密切 [
老鸦巢矿区内铅锌矿物多与金属硫化物共生,并且在岩石、矿石或矿物裂隙中常充填有石英、方解石等。金属硫化物常以单矿物脉或条带状、不规则状多金属组合脉出现,本次实验主要以黄铁矿和闪锌矿为观察对象。
本区黄铁矿发育有早、中、晚三个阶段,在矿石中的分布主要呈自形或半自形粒状分布。早期生成的黄铁矿其颗粒较大,1~3 mm,晶形多呈五角十二面体,少量为立方体。中期生成的黄铁矿颗粒较细,0.5~1.5 mm,晶形多呈半自形或它形。晚期生成少量黄铁矿呈球状、草莓状、胶状,分布在裂隙中。根据野外调查和室内矿相学显微境下观察分析,认为本区黄铁矿的结构类型主要为(图2):①自形粒状结构、②半自形–他行粒状结构、③裂隙充填结构、④包含结构、⑤交代残余结构、⑥骸晶结构、⑦交错结构;而其组合类型可分为如下四种:以黄铁矿–黄铜矿–磁铁矿、黄铁矿–方解石、黄铁矿–闪锌矿–黄铜矿、黄铁矿–方铅矿。
矿区的闪锌矿同样可分为早、中、晚三个时期,在矿石中主要呈自形或半自形–它形粒状分布,粒径0.5~1 mm。早期生成的闪锌矿颜色较深,为褐黑色,颗粒较粗,自形程度高;中期生成颜色较深,棕褐色,颗粒较细的闪锌矿;晚期生成的闪锌矿颜色浅,松香色或浅棕色,少部分为深红色,沿裂隙、空洞充填,呈葡萄状的集合体与八面体方铅矿共生。根据野外调查和室内矿相学显微境下观察分析,认为本区闪锌矿的共生组合可分为:闪锌矿–黄铁矿、闪锌矿–黄铜矿–黄铁矿两种组合类型;其结构类型可分为如下5种(图3):①自形粒状结构、②半自形–他形粒状结构、③乳滴状结构、④叶片状结构、⑤交代结构。
矿石样品矿石样品采自老鸦巢矿区9中段、13中段,多为块状矿石。电子探针原位微区元素定量分
(a) 黄铁矿自形粒状结构;(b) 黄铁矿骸晶结构;(c) 黄铁矿裂隙充填结构;(d) 黄铁矿交代残余结构
(a) 闪锌矿半自形–他形粒状结构;(b) 闪锌矿与黄铁矿交代结构;(c) 闪锌矿中黄铜矿呈乳滴状结构;(d) 闪锌矿中黄铜矿呈叶片状结构
析测试工作是在中南大学地球科学与信息物理学院的电子探针微区分析实验室(教育部有色金属成矿预测重点实验室)完成。应用日本岛津公司生产的EPMA-1720型电子探针(EPMA),加速电压(acc.voltage)选择为15 kV,电子束流(probe current)大小为10 nA,束斑大小为1 μm,检出限0.01%,校正方法为ZAF校正。本次实验对黄铁矿测试元素有As、S、Fe、Co、Pb、Ni、Cu、Zn 8种元素;闪锌矿测试元素有Ga、S、Mn、Ge、Cd、Fe、Se、In和Zn共9种元素。
老鸦巢矿区黄铁矿电子探针原位微区元素定量分析测试结果见表1。测试结果显示,黄铁矿测试的元素中,Pb、Co、Ni、Cu和Zn等部分含量低于检测限,S、Fe、As等含量均高于超过检测限。矿区黄铁矿的S元素含量范围为51.29%~53.61%,平均为52.56%,Fe元素含量范围为44.78%~48.16%,平均为46.51%,Pb元素含量范围为0%~1.18%,As元素含量范围为0.11%~0.30%,平均为0.19%。Co的含量为0.01%~0.21%,平均为0.06%,可Ni的含量比较低,只在样品局部可以检测到,其含量范围变化为0.00%~0.14%。
矿区闪锌矿电子探针原位微区元素定量分析测试结果见表2。测试结果显示,除了Zn、S元素外,还有Fe以及微量的Mn、Ge、Cd、Se、In等元素。所有测量点的Ga含量均低于检测限,一部分测量点的Ge、Se、In的含量也低于检测限,其他元素Zn、S、Mn、Cd含量均高于检测限。老鸦巢铅锌矿床闪锌矿的S元素的含量范围为31.84%~32.49%,平均值32.21%,Zn的含量变化范围为62.82%~64.66%,平均值为63.54%,Cd的含量变化范围为0.46%~0.55%,平均值为0.50%,Fe元素的变化范围是2.41%~3.34%,平均值为2.75%。
黄铁矿理论上Fe、S的含量分别为46.55%、53.45%,S/Fe的值为2 (原子量比)。徐国风等(1980) [
黄铁矿中的一些微量元素,也有各自的标型意义。其Co、Ni的比值就有指示成因的作用。比如与中基性岩浆热液和火山作用有关的高温岩浆热液矿床形成的黄铁矿,其Co/Ni大于1;沉积成因形成的黄铁矿中,其Co/Ni小于1;由于热液改造程度的不同,与火山作用有关的层控矿床Co/Ni的比值有大有小 [
样号 | 序号 | As | S | Fe | Pb | Co | Ni | Cu | Zn | Total | S/Fe | Co/Ni |
---|---|---|---|---|---|---|---|---|---|---|---|---|
SKS-1 | 1 | 0.11 | 51.98 | 44.78 | 1.18 | 0.09 | - | 0.03 | 0.05 | 98.23 | 2.02 | |
2 | 0.24 | 52.63 | 45.79 | 1.00 | 0.06 | - | 0.08 | - | 99.80 | 2.00 | ||
3 | 0.23 | 52.85 | 46.21 | 0.65 | 0.02 | - | - | - | 99.96 | 1.99 | ||
4 | 0.16 | 52.62 | 45.13 | 0.67 | 0.06 | 0.01 | 0.03 | 0.09 | 98.75 | 2.03 | 6.00 | |
5 | 0.17 | 52.97 | 46.22 | 0.23 | 0.07 | - | - | - | 99.66 | 2.00 | ||
6 | 0.21 | 52.51 | 45.45 | 0.84 | 0.05 | - | 0.01 | 0.01 | 99.08 | 2.01 | ||
7 | 0.16 | 52.26 | 45.76 | 0.64 | 0.03 | 0.01 | - | 0.08 | 98.93 | 1.99 | 3.00 | |
8 | 0.22 | 52.36 | 45.79 | 0.49 | 0.09 | 0.02 | 0.02 | 0.04 | 99.02 | 1.99 | 4.50 | |
9 | 0.18 | 52.93 | 45.77 | 0.53 | 0.01 | 0.06 | 0.02 | 0.02 | 99.53 | 2.01 | 0.17 | |
10 | 0.23 | 52.09 | 45.67 | 0.50 | 0.04 | 0.04 | 0.03 | 0.01 | 98.61 | 1.99 | 1.00 | |
11 | 0.16 | 52.40 | 45.31 | 1.05 | 0.06 | - | - | 0.02 | 99.01 | 2.01 | ||
12 | 0.15 | 51.92 | 44.86 | 1.10 | 0.03 | - | 0.01 | - | 98.07 | 2.02 | ||
SKS-2 | 13 | 0.15 | 53.09 | 46.95 | - | 0.04 | - | - | - | 100.23 | 1.97 | |
14 | 0.13 | 52.96 | 47.19 | - | 0.04 | 0.07 | 0.09 | - | 100.47 | 1.95 | 0.57 | |
15 | 0.20 | 52.80 | 47.62 | - | 0.10 | - | 0.08 | 0.09 | 100.89 | 1.93 | ||
16 | 0.11 | 53.61 | 46.82 | - | 0.02 | 0.04 | - | - | 100.60 | 1.99 | 0.50 | |
17 | 0.19 | 53.11 | 46.75 | - | 0.12 | - | 0.08 | 0.01 | 100.26 | 1.98 | ||
18 | 0.21 | 53.25 | 46.98 | - | 0.03 | - | 0.04 | - | 100.50 | 1.97 | ||
19 | 0.12 | 52.43 | 48.16 | - | 0.06 | 0.02 | - | - | 100.79 | 1.90 | 3.00 | |
20 | 0.18 | 53.22 | 46.89 | - | 0.05 | 0.04 | 0.01 | 0.12 | 100.51 | 1.98 | 1.25 | |
21 | 0.20 | 53.37 | 47.37 | - | 0.07 | 0.06 | 0.02 | 0.08 | 101.18 | 1.96 | 1.17 | |
22 | 0.21 | 53.39 | 47.00 | - | 0.05 | - | 0.04 | 0.06 | 100.74 | 1.98 | ||
SKS-10 | 23 | 0.16 | 52.77 | 47.03 | - | 0.02 | - | - | 0.06 | 100.03 | 1.95 | |
24 | 0.17 | 52.99 | 47.35 | - | - | 0.01 | 0.02 | - | 100.54 | 1.95 | ||
25 | 0.19 | 52.09 | 47.13 | - | 0.07 | 0.14 | 0.09 | 0.08 | 99.79 | 1.93 | 0.50 | |
26 | 0.14 | 52.34 | 46.56 | - | 0.08 | - | - | 0.09 | 99.20 | 1.96 | ||
27 | 0.16 | 52.98 | 47.02 | - | 0.02 | 0.07 | 0.06 | 0.03 | 100.34 | 1.96 | 0.29 | |
28 | 0.25 | 52.76 | 47.30 | - | 0.08 | - | - | 0.08 | 100.47 | 1.94 | ||
29 | 0.22 | 53.04 | 47.15 | - | 0.09 | 0.06 | 0.02 | 0.10 | 100.67 | 1.96 | 1.50 | |
ZK2071-5 | 30 | 0.25 | 51.41 | 46.34 | 0.21 | 0.10 | - | - | 0.01 | 98.32 | 1.93 | |
31 | 0.30 | 52.20 | 46.48 | 0.41 | 0.12 | - | 0.04 | - | 99.55 | 1.96 | ||
32 | 0.21 | 51.29 | 45.91 | 0.42 | 0.21 | 0.09 | 0.07 | - | 98.20 | 1.95 | 2.33 | |
33 | 0.17 | 52.19 | 46.46 | 0.05 | 0.03 | - | 0.11 | 0.01 | 99.02 | 1.96 | ||
34 | 0.26 | 52.05 | 48.03 | 0.04 | 0.12 | - | 0.11 | 0.01 | 100.62 | 1.89 | ||
35 | 0.21 | 51.35 | 46.77 | 0.33 | 0.13 | 0.04 | - | 0.03 | 98.86 | 1.91 | 3.25 | |
36 | 0.26 | 51.98 | 46.36 | 0.01 | 0.06 | 0.14 | - | - | 98.80 | 1.95 | 0.43 |
表1. 老鸦巢铅锌矿床黄铁矿电子探针微区成分分析结果(%)
测试单位:中南大学有色金属成矿预测与地质环境监测教育部重点实验室电子探针分析实验室;“-”表示元素的含量低于检测限。
样号 | 序号 | Ga | S | Mn | Ge | Cd | Fe | Se | In | Zn | Total | S/Zn | FeS分子数(%) |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
SKS-10 | 1 | - | 32.49 | 0.15 | - | 0.50 | 3.34 | 0.01 | 0.02 | 63.06 | 99.56 | 1.05 | 5.84 |
2 | - | 32.35 | 0.13 | - | 0.49 | 2.41 | 0.01 | 0.05 | 63.80 | 99.23 | 1.03 | 4.24 | |
3 | - | 32.43 | 0.10 | 0.02 | 0.55 | 2.74 | - | 0.03 | 63.64 | 99.50 | 1.04 | 4.80 | |
4 | - | 31.97 | 0.12 | 0.03 | 0.46 | 2.61 | 0.03 | 0.02 | 64.66 | 99.90 | 1.01 | 4.51 | |
5 | - | 32.02 | 0.06 | 0.03 | 0.46 | 2.74 | 0.02 | 0.01 | 63.50 | 98.82 | 1.03 | 4.81 | |
6 | - | 32.26 | 0.09 | 0.01 | 0.50 | 2.77 | 0.04 | 0.01 | 63.42 | 99.11 | 1.04 | 4.87 | |
7 | - | 32.29 | 0.09 | 0.04 | 0.51 | 2.66 | - | 0.03 | 64.15 | 99.76 | 1.03 | 4.62 | |
8 | - | 32.07 | 0.10 | - | 0.55 | 2.75 | - | - | 63.32 | 98.79 | 1.03 | 4.83 | |
9 | - | 31.84 | 0.10 | - | 0.46 | 2.80 | 0.02 | 0.01 | 62.82 | 98.03 | 1.03 | 4.95 | |
10 | - | 32.34 | 0.09 | - | 0.52 | 2.65 | 0.03 | - | 62.99 | 98.63 | 1.05 | 4.70 |
表2. 老鸦巢铅锌矿床闪锌矿电子探针微区成分分析结果(%)
测试单位:中南大学有色金属成矿预测与地质环境监测教育部重点实验室电子探针分析实验室;“-”表示元素的含量低于检测限。
与小于1的类型都存在,其成因类型就难以做出较为准确的判断。但是,Bralia et al. (1979) [
As的晶体化学性质和S相似,一般会在黄铁矿中以类质同象替换S,所以黄铁矿中As的含量往往对其成因也具有一定指示意义。鲍正襄等(2002) [
严育通等(2012) [
综上研究,认为老鸦巢铅锌矿床黄铁矿的Fe/S取值范围为0.858~0.923,平均值为0.885,大于黄铁矿Fe/S的理论值(0.875)。因此,认为本区的黄铁矿是具富铁贫硫特征,且形成于中低温热液环境。
闪锌矿在理论上Zn的含量67.10%,S的含量为32.90%,S/Zn = 1(原子量比)。S、Zn含量的变化,和其比值的变化程度,对闪锌矿的成因类型都有重要的指示意义。本次检测的样品中S/Zn的比值变化范围为1.01~1.05,平均值为1.03,均大于闪锌矿中S/Zn的理论原子比,表明了老鸦巢矿区闪锌矿形成于硫逸度较高的热液环境 [
研究表明,共生的闪锌矿与黄铁矿,可利用FeS含量来估算成矿温度范围 [
(a) Co与As的关系图;(b) Pb与Fe的关系图;(c) As与S的关系图;(d) Ni与Co的关系图
式中w(Fe),w(Zn)分别表示闪锌矿中Fe和Zn的含量(%);Ar(Fe),Ar(Zn)表示Fe和Zn的相对原子量。
从图5中可以看出,老鸦巢铅锌矿床闪锌矿10个点落入有效位置上,对应温度为170˚C~220˚C,指示闪锌矿的成矿温度属于中温。
闪锌矿中的微量元素对判别矿床成因有重要的指示意义。张乾(1987) [
老鸦巢铅锌矿床闪锌矿中Cd的含量范围为0.46%~0.55%,平均值为0.50%。元素Cd与Zn有相似的地球化学性质,一般以类质同像替代Zn,保持一定的含量存于闪锌矿中 [
图5. 老鸦巢闪锌矿中FeS含量与温度关系 [
(1) Cd与Zn/Cd的关系图;(2) Fe与Zn的关系图;(3) Cd与Fe的关系图;(4) Cd与Zn的关系图
该特征和典型的岩浆热液矿床中矽卡岩的闪锌矿特征比较类似 [
刘英俊(1984) [
1) 本区黄铁矿从早到晚阶段自形程度变差,由自形粒状到半自形–他形粒状分布,粒径0.5~3 mm,晶形多呈五角十二面体,少量为立方体,局部矿物裂隙中生成球状、草莓状、胶状等黄铁矿颗粒。闪锌矿主要呈自形或半自形–它形粒状分布,粒径0.5~1 mm,从早到晚其颜色逐渐变浅,自形程度变差,晚期闪锌矿沿裂隙、空洞充填,呈葡萄状的集合体与八面体方铅矿共生。
2) 黄铁矿中Co与As呈正相关性,Co与Ni含量变化有较为明显正相关性,而As与S含量变化成明显的负相关,表明Co、As、Ni是以类质同象替换S进入黄铁矿内;Pb与Fe含量变化为十分明显负相关关系,表明Pb是以类质同象替换Fe元素赋存黄铁矿内部。
3) 闪锌矿中Cd与Fe呈不明显的正相关性,Cd与Zn呈负相关性,Fe与Zn呈负相关性,表明本区Cd、Fe进入闪锌矿的主要方式为类质同象替代Zn。
4) 经过黄铁矿和闪锌矿电子探针成分分析,认为区内黄铁矿具弱亏硫不亏铁特征,Co/Ni比值变化大,平均值大于1,As含量高于其他微量元素,综合认为其形成于中低温热液环境下;区内闪锌矿富硫亏锌,且w(Mn) < 0.15%、w(Fe) < 6%、Ga/In < 1、Zn/Cd在114~140之间,Cd的含量与Zn/Cd的值呈很明显的负相关性,同时FeS分子投图对应温度为170˚C~220˚C,共同显示了闪锌矿具有中低温岩浆热液成因的特征。
本次研究工作得到了中南大学“创新驱动项目”的资助,野外工作得到了刘忠法老师及刘清泉博士帮助和指导,测试工作得到了中南大学有色金属成矿预测与地质环境监测教育部重点实验室电子探针分析实验室大力支持,在此一并表示感谢。论文撰写期间程路平、言奇等人提供有益的建议,在此予以致谢。
中南大学“创新驱动项目”(2015CX008)。
冯玉龙,邵拥军,蒋梦同,冯雨周,宋泽友. 湖南省老鸦巢铅锌矿床金属硫化物微区成分特征 Micro Area Composition Characteristics of Metal Minerals in the Laoyachao Pb-Zn Deposit in Hunan Province[J]. 地球科学前沿, 2017, 07(04): 574-585. http://dx.doi.org/10.12677/AG.2017.74059