为探究粉末尺寸对稀土铬氧化物的结构、磁性的影响机制,我们用溶胶凝胶法成功制备出不同尺寸的YbCrO 3粉末样品。结构和磁性的研究表明晶胞体积随着粉末尺寸的增大而减小,同时Cr-O键长基本不变,而Cr-O-Cr键角逐渐减小,且制备的粉末尺寸随着烧结温度的升高而逐渐增大。Cr-O-Cr键角对YbCrO 3粉末的磁性影响反应在随着粉末尺寸的增大,热磁曲线上T comp、T max、M max明显增大及奈尔温度T N微弱增大。一方面,Cr-O-Cr键角的减小削弱Cr 3+离子之间的反铁磁耦合强度;另一方面,其长程有序度逐渐提高增强Cr 3+离子之间的反铁磁耦合强度。二者的竞争关系使得T N随着粉末尺寸的增大而轻微增大。同时M-T曲线的拟合结果也表明,在T N以下,Cr-O-Cr键角的减小和长程序的提高增强了Cr 3+-O 2−-Cr 3+超交换作用,提高了Cr 3+的净磁矩M Cr及Cr 3+对Yb 3+作用的内场H I。低温下的磁滞回线表明粉末样品的正向交换偏置场随着Cr-O-Cr键角减小而增大。 In order to explore the influence of structure and magnetism of rare earth chromium oxide from powder size, YbCrO 3 powder samples with different sizes were successfully fabricated by sol-gel method. The studies of structure indicate that the size of powder increases with the increase of sintering temperature, and cell volume and Cr-O-Cr bond angle decrease with the increase of powder size, while the Cr-O bond length is nearly unchanged. The effection of Cr-O-Cr bond angle on the magnetic properties of YbCrO 3 powder was reflected on the obvious increase of T comp, T max and M max and weak increase of Neil temperature T N in thermomagnetic curves with the increase of powder size. On the one hand, the decrease of the Cr-O-Cr bond angle weakened the an-ti-ferromagnetic coupling strength between Cr 3+ ion; on the other hand, the gradually increase of long range order enhanced the anti-ferromagnetic coupling strength between Cr 3+ ion. The com-petition made the T N slightly increase with the increase of the powder size. The M-T curve fitting results also showed that, under T N, the decrease of the Cr-O-Cr bond angle and the increase of long range order enhanced the Cr 3+-O 2−-Cr 3+ superexchange effect, improved the net magnetic moment of Cr 3+ (M Cr) and the infield of Yb 3+ from Cr 3+ (H I). The low temperature hysteresis loop showed that positive exchange bias field increased with the decreases of Cr-O-Cr bond angle.
毛耀文,王瑞龙,张城城
湖北大学物电学院,湖北 武汉
收稿日期:2018年7月26日;录用日期:2018年8月7日;发布日期:2018年8月14日
为探究粉末尺寸对稀土铬氧化物的结构、磁性的影响机制,我们用溶胶凝胶法成功制备出不同尺寸的YbCrO3粉末样品。结构和磁性的研究表明晶胞体积随着粉末尺寸的增大而减小,同时Cr-O键长基本不变,而Cr-O-Cr键角逐渐减小,且制备的粉末尺寸随着烧结温度的升高而逐渐增大。Cr-O-Cr键角对YbCrO3粉末的磁性影响反应在随着粉末尺寸的增大,热磁曲线上Tcomp、Tmax、Mmax明显增大及奈尔温度TN微弱增大。一方面,Cr-O-Cr键角的减小削弱Cr3+离子之间的反铁磁耦合强度;另一方面,其长程有序度逐渐提高增强Cr3+离子之间的反铁磁耦合强度。二者的竞争关系使得TN随着粉末尺寸的增大而轻微增大。同时M-T曲线的拟合结果也表明,在TN以下,Cr-O-Cr键角的减小和长程序的提高增强了Cr3+-O2−-Cr3+超交换作用,提高了Cr3+的净磁矩MCr及Cr3+对Yb3+作用的内场HI。低温下的磁滞回线表明粉末样品的正向交换偏置场随着Cr-O-Cr键角减小而增大。
关键词 :稀土铬氧化物,氧空位,超交换作用,负磁化,交换偏置
Copyright © 2018 by authors and Hans Publishers Inc.
This work is licensed under the Creative Commons Attribution International License (CC BY).
http://creativecommons.org/licenses/by/4.0/
纳米材料具有低维度、量子效应,且其结构、磁性与纳米粉末的尺寸都具有独特的依赖机制,因而研究的热点逐渐转向纳米尺寸的钙钛矿结构氧化物 [
这些应用在锰氧化物的纳米粉末的制备方法和纳米尺寸差异对样品的结构、磁性的影响机制同样在部分的稀土铬氧化物中也有过报道。在DyCrO3 [
在本文中,我们通过控制烧结温度来制备不同尺寸的YbCrO3纳米粉末,并对样品的结构、磁性与纳米尺寸的依赖关系进行了系统研究,以期待为探究纳米尺寸粉末尺寸对稀土铬氧化物的结构、磁性的影响机制提供有价值的参考。
本文采用溶胶–凝胶法在750℃、950℃、1150℃、1350℃烧结温度下制备了相应4个不同粉末尺寸粉末样品。首先根据所需样品的金属离子的化学摩尔比例及柠檬酸与金属阳离子的摩尔比为2:1,计算并精确称量高纯度的Cr(NO3)3∙9H2O (>99.99%)、Yb(NO3)3∙5H2O (>99.0%)及柠檬酸。混合搅拌硝酸盐溶液并将柠檬酸溶液逐滴加入混合溶液直至搅拌均匀。在80℃下搅拌水浴直至形成胶状、无流动性的凝胶。然后将其置于控温电热套中,经低温燃烧充分得到呈褐色粉末前躯体。将前躯体研磨均匀并经过两次500℃保温1 h的预烧。最后把预烧后的粉末研磨均匀,分别在750℃、950℃、1150℃、1350℃下保温5 h进行烧结,制备出4个不同粉末尺寸粉末样品。使用X射线衍射仪(XRD,Bruker公司,D8)对样品晶体结构进行分析;使用扫描电镜(SEM,JEOL公司,JSM-7100F)完成样品形貌采集。使用超导量子干涉仪(SQUID-VSM, Quantum Design)对样品进行磁性分析。
图1为各YbCrO3样品的XRD测试精修图,样品测试数据的分析结果表明样品成相良好,无杂相,均为正交钙钛矿结构,且空间群为Pbnm。表1为Rivetved精修的具体结果列表。由表可看出晶格参数a呈现减小趋势,而b、c呈现锯齿形变化趋势,这是因为烧结效应增强了晶胞的在不同方向上的畸变效应。
图1. YbCrO3粉末样品的XRD结果精修图
YbCrO3 | 750℃ | 950℃ | 1150℃ | 1350℃ |
---|---|---|---|---|
a(Å) | 5.50785(19) | 5.50580(23) | 5.50481(17) | 5.50470(14) |
b(Å) | 7.49559(26) | 7.49239(31) | 7.49246(23) | 7.49187(18) |
c(Å) | 5.19909(20) | 5.19703(24) | 5.19741(17) | 5.19774(14) |
V(Å) | 214.642(13) | 214.386(16) | 214.365(12) | 214.357(73) |
θ(Cr-O(1)-Cr) | 147.442(1) | 141.734(1) | 142.753(1) | 141.908(1) |
θ(Cr-O(2)-Cr) | 145.160(2) | 148.342(2) | 146.274(1) | 146.888(1) |
θ ( Cr-O-Cr ) ¯ | 146.301 | 145.038 | 144.513 | 144.398 |
Length Cr-O(1) | 1.98637(5) 1.95904(5) | 2.02723(6) 1.97967(6) | 1.99519(5) 1.99934(5) | 2.03276(4) 1.97193(4) |
Length Cr-O(2) | 1.96413(6) | 1.94693(7) | 2.00881(4) | 1.95398(4) |
Length Cr-O ¯ | 1.969847 | 1.98461 | 2.001115 | 1.986223 |
D(nm) | ~120 | ~210 | ~310 | ~370 |
表1. YbCrO3的XRD精修结果列表
同时高温烧结使其结合更紧致,使晶格体积随烧结温度升高而收缩。晶胞格畸变变化的不确定性使晶胞内Cr3+-O-Cr3+键角及Cr-O键长随烧结温度升高而呈现锯齿状变化,但平均键长变化量较小,几乎保存一个稳定值~1.985,且其Cr3+-O-Cr3+键角的平均值呈现减小趋势。图2为粉末样品的SEM微观形貌(左图所示)及随机对100个个单个纳米粉末的尺寸统计并拟合(右图所示),其结果表明YbCrO3纳米粉末的尺寸D分别为~120 nm、~210 nm、~310 nm、~370 nm,随烧结温度升高而增大。这是在奥斯瓦尔德熟化效应的作用下,随着烧结温度改变粉粉末的团聚程度,因而纳米粉末尺寸随烧结温度升高而增大。
图3为样品的场冷却(Field-cooling, FC)下的热磁曲线。可以看出所有样品体系的热磁曲线的变化趋势基本一致,磁化强度均在TN开始增大并在Tmax处达到最大值Mmax,然后减小,在低于补偿温度(Tcomp)出现负磁化效应,磁化曲线的明显变化预示这形成带着弱铁磁矩的倾角反铁磁有序。尺寸会引起TN变化,在曾报道粉末尺寸为60~425 nm的HoCrO3 [
为了研究粉末样品中的Cr3+对Yb3+作用的内场与Cr-O-Cr键角依赖关系,我们把场冷热磁曲线用M = MCr + C(HI + Hmeas)/(T − θ)公式拟合,其中MCr、C、HI和θ分别是Cr3+的自旋磁矩、居里常数、内场和Yb3+的外斯温度。具体结果如图4所示,图中拟合曲线和热磁曲线很好吻合,其具体拟合参数如表3所示。随着Cr-O-Cr键角减小,MCr呈现增大趋势,这与Mmax、Tmax的变化趋势相符合。同时HI的负值吻合了内场方向与冷场H方向相反;随着Cr-O-Cr键角减小,HI在4800 Oe~6600 Oe之间呈现的增大趋势证实了Cr3+对Yb3+施加的内场作用和Cr-O-Cr键角的关联性。
图2. SEM图像及对应的统计拟合结果:750℃ (a, e),950℃ (b, f),1150℃ (c, g),1350℃ (d, h)
图3. YbCrO3在100 Oe下的场冷热磁曲线
图4. YbCrO3场冷热磁曲线的拟合图
750℃ | 950℃ | 1150℃ | 1350℃ | |
---|---|---|---|---|
Tcomp (K) | 13.03 | 14.42 | 17.36 | 17.79 |
Tmax (K) | 66.94 | 68.96 | 70.95 | 72.99 |
Mmax (emu/g) | 0.4728 | 0.5934 | 0.6286 | 0.6635 |
表2. YbCrO3的Tmax、Mmax、Tcomp参数列表
750℃ | 950℃ | 1150℃ | 1350℃ | |
---|---|---|---|---|
MCr (emu/mol) | 245.10 | 313.37 | 360.53 | 390.25 |
HI (Oe) | −4862.2 | −5548.0 | −6235.5 | −6572.6 |
θ (K) | −26.599 | −25.78932 | −25.91039 | −26.504 |
C | 1.9437 | 2.2237 | 2.5043 | 2.6419 |
表3. YbCrO3场冷模式下热磁曲线的拟合结果参数
图5. T = 5 K时YbCrO3的磁滞回线;插图为低场区域放大图
为进一步探究研究样品低温下的磁性与Cr-O-Cr键角的依赖关系,测量了各样品在5 K下的等温磁化M-H曲线,结果如图5所示。可以观察到各曲线趋势一致且均出现正向交换偏置效益,表明此时样品中Yb3+-Yb3+的相互作用取代Cr3+-O2−-Cr3+倾角反铁磁作用并占据主导地位。同时饱和磁化强度随烧结温度升高而增大,这很好地与吻合M-T曲线拟合结果相吻合。随着键角减小,样品的正向交换偏置场偏移量增大(如插图(b)所示),这源于粉末样品中的Cr3+对Yb3+作用内场的增大,因而Yb离子磁矩反转需更高外场诱导,使正偏移量增大。插图(a)为各样品在50 K的磁滞回线部分放大图,纳米粉末的长程有序性容易被破坏,使样品在不同温度烧结下产生不同浓度的氧空位,从而样品出现一定程度的Cr2+削弱超交换作用并且出现Cr2+和Cr3+/Yb3+之间的相互作用,这些影响着反铁磁态和倾角弱铁磁态共存的温度,其随烧结温度升高而增大。因而在750℃、950℃烧结的样品同时出现磁滞和负交换偏置效应,且750℃烧结的样品磁滞更为明显。对于1150℃和1350℃烧结的样品仅出现负交换偏置效应。
我们利用溶胶–凝胶法在不同温度下烧结制备了YbCrO3纳米粉末样品,并研究其结构及磁性。XRD数据及其结构精修结果表明晶胞体积随着烧结温度的升高而减小,Cr-O键长基本不变,而Cr-O-Cr键角逐渐减小。SEM图像及粉末尺寸统计拟合结果表明粉末尺寸随着烧结温度的升高而逐渐增大。随着粉末尺寸的增大,Cr-O-Cr键角的减小,而Cr-O-Cr键角的减小引起D-M相互作用变化,增强了倾斜的弱铁磁性,进而提高了Cr3+对Yb3+作用的内场HI大小,相应地,样品最大磁矩温度Tmax、补偿温度Tcom也随之逐渐降低。这一点从M-T曲线也得到验证。低温(5 K)的磁滞回线测量表明,样品均表现为正向交换偏置效应,同时,可以看到交换偏置场随样品中Cr-O-Cr键角的减小和Cr-O-Cr组分的增多而增大。这些研究有利于深入理解稀土铬氧化物磁相互作用的物理机制,并对其物理效应进行有效调控,有助于稀土铬氧化物在磁电子器件中应用。未来,我们将探讨其他稀土铬氧化物体系的结构和性质,如在TmCrO3体系参杂,期望对稀土铬氧化物磁相互作用的物理机制有更深入、更广泛的认识,并探寻更普遍的调控手段,将稀土铬氧化物应用于磁电子器件中。
湖北省自然科学基金(No. 2015CFB549)。
毛耀文,王瑞龙,张城城. YbCrO3纳米粉末的制备及其结构和磁性的研究 The Preparation of YbCrO3 Nanometer Powder and the Study of Its Structure and Magnetism[J]. 凝聚态物理学进展, 2018, 07(03): 90-98. https://doi.org/10.12677/CMP.2018.73012