Material Sciences
Vol.07 No.02(2017), Article ID:20114,6 pages
10.12677/MS.2017.72030

Thermodynamics Analysis on BaF2 Intermediate Phase in Solution-Derived YBCO Superconducting Film Deposition

Hongyuan Lu1, Feng Feng1, Wei Wu2*, Xiangsong Zhang1, Linli Wang1, Timing Qu3, Shengjun Zhai4, Pingfa Feng1

1Division of Advanced Manufacturing, Graduate School at Shenzhen, Tsinghua University, Shenzhen Guangdong

2Department of Electrical Engineering, Shanghai Jiao Tong University, Shanghai

3Department of Mechanical Engineering, Tsinghua University, Beijing

4Beijing Eastforce Superconducting Technology Co., Ltd., Beijing

Received: Mar. 19th, 2017; accepted: Mar. 28th, 2017; published: Mar. 31st, 2017

ABSTRACT

In the YBa2Cu3O7-δ (YBCO) high temperature superconducting thin film fabrication via the chemical solution deposition method, BaF2 is an important intermediate phase during heat treatment. In this paper, BaF2 thermodynamics stability was analyzed through calculating the standard Gibbs free energy change (ΔGT) of the reactions related to other intermediate phases within the temperature range of 700 - 1000 K. Two thermodynamics methods, the Gibbs free energy function method and standard formation molar Gibbs free energy method, were utilized to obtain the ΔGT values. This study confirms the formation priority of BaF2 relative to other mesophase at high temperatures while the possibility of BaCO3 formation was found at 700 K.

Keywords:High Temperature Superconducting, Thin Film Deposition, Standard Gibbs Free Energy Change

钇钡铜氧超导膜溶液法沉积过程中氟化钡中间相的热力学分析

卢弘愿1,冯峰1,吴蔚2*,张向松1,汪林立1,瞿体明3,翟胜军4,冯平法1

1清华大学深圳研究生院先进制造学部,广东 深圳

2上海交通大学电气工程系,上海

3清华大学机械工程系,北京

4北京原力辰超导技术有限公司,北京

收稿日期:2017年3月19日;录用日期:2017年3月28日;发布日期:2017年3月31日

摘 要

在使用化学溶液沉积技术制备钇钡铜氧高温超导薄膜的过程中,氟化钡是一种重要的热处理中间相。在本文中,通过对氟化钡向其他中间相转化的化学反应进行标准吉布斯自由能变计算,对氟化钡的热力学稳定性进行了分析,考虑的温度范围为700至1000开尔文。计算中使用了物质吉布斯自由能函数法和物质生成标准摩尔吉布斯自由能法两种方法,计算标准吉布斯自由能变。该研究验证了氟化钡在较高温度下相对于其他中间相的生成优先性,同时也发现了700开尔文下碳酸钡相生成的可能性。

关键词 :高温超导,薄膜沉积,标准吉布斯自由能变化

Copyright © 2017 by authors and Hans Publishers Inc.

This work is licensed under the Creative Commons Attribution International License (CC BY).

http://creativecommons.org/licenses/by/4.0/

1. 引言

REBa2Cu3O7-δ (REBCO,RE代表稀有稀土元素包括钇、钆、钐等)高温超导(HTS)材料在许多领域有重要应用前景 [1] [2] 。在众多的制备技术中,化学溶液沉积法(CSD)具有成本低、均匀性好、沉积速率快、可精确控制最终产物成分等优点,因此在国内外的产业化中都备受重视。含三氟乙酸前驱溶液(TFA)被广泛用于钇钡铜氧(YBCO)高温超导薄膜的制备的金属有机沉积(MOD)路线当中 [3] [4] 。在MOD-YBCO过程中,前驱溶液涂覆在基底上进行热处理,热处理过程包括热解、结晶和充氧三个步骤 [5] [6] 。热解步骤结束后,有机前驱盐分解为中间相,中间相随着温度的升高而演化,之后在结晶步骤中反应生成YBCO相。在各类中间相中,BaCO3是认为是有害的,因为它在结晶温度下很稳定,会降低最终的YBCO薄膜的超导性能,而BaF2一般被认为是能够抑制BaCO3形成的中间相 [6] [7] 。而探索中间相的转化机制可以为连续调节氟钡比制备YBCO厚膜的研究提供支持。

在Clem的研究 [8] 中,使用ThermocalcTM软件对钙钛矿系统中BaCO3/BaF2/BaTiO3的热力学稳定性进行了计算,在0℃ - 1000℃温度范围内BaF2被预计具有比BaCO3更强的稳定性。在本研究中,通过考察可能的中间相转化反应来计算BaF2的稳定性,并涉及其它的中间相如YF3和CuO。为了更进一步了解BaF2相关的反应,采用两种计算方式来计算标准吉布斯自由能变化(ΔGT),考察的温度(T)为700, 800, 900和1000 K,这些温度均在中间相演化范围内。

2. 分析方法

2.1. 中间相转化反应

为了研究BaF2的热力学稳定性,氟钡相关相将会作为可能的中间相,包括BaO, BaCO3, Ba(OH)2, YF3和CuF2。值得注意的是还有Y2Cu2O5,Ba1-xYxF2+x,Ba-O-F [5] [6] 等其它相关中间相。由于这些中间相的热力学数据手册上查不到,因此本研究中不涉及这些中间相。可能涉及上述中间相的转化反应概括如表1。一个反应的ΔGT值如果为正数且较大则表明反应不能在标准条件下发生。因此,列表中ΔGT的计算结果可以被用来解释BaF2转化反应发生的可能性,并近一步探讨BaF2在中间相演化中的生成优先性。在本研究中,使用了物质吉布斯自由能函数法和物质生成标准摩尔吉布斯自由能方法两套计算体系。

2.2. 物质吉布斯自由能函数法

叶大伦 [9] 介绍的物质吉布斯自由能函数法原理是将反应吉布斯自由能变ΔGT的计算变为物质i(方程式中的化学计量系数ni)的吉布斯自由能函数ϕi,T以及标准摩尔生成焓∆Hi,f,298的计算,如公式1-3所示。

反应(a)-(g)所涉及的φi,T and ΔHi,f,298数据可以在参考文献中找到 [9] 。值得注意的是(表2),Ba(OH)2熔点为681 K,而手册中的ϕT只有298 - 681 K之间的固态数据,因此高温度的液态数据我们使用了已有数据的线性外推结果替代,可能会造成计算结果与真实情况存有一定偏差,下文中将进行相关的讨论。

(1)

(2)

(3)

2.3. 物质生成标准摩尔吉布斯自由能法

不同温度下的物质生成标准摩尔吉布斯自由能∆Gf,T也可以很方便的在热力学手册中查到,计算过程

Table 1. Possible conversion reactions of BaF2

表1. 可能发生的BaF2转化反应

Table 2. Gibbs free energy functionφi,T and standard molar formation enthalpy ΔHi,f,298 in reference [9] , the unit is J∙mol−1

表2. 相关物质的标准摩尔生成焓∆Hi, f,298和吉布斯自由能函数φi,T,其中T(单位K)表示反应的温度,所有数据均以J∙mol−1为单位 [9]

如方程(4)所示 [11] ,相关相的∆Gf,T值引用了参考文献 [11] ,如表3所示。

(4)

3. 结果与讨论

3.1. 用两种方法计算的温度依赖的吉布斯自由能变化结果比较

表1中的反应的吉布斯自由能变化(ΔGT)使用上面提到的两种方法进行计算,得到的结果分别在表4表5列出。

表4表5中的ΔGT数据对照在图1中进行比较分析,可以看到,用两种不同计算方法得到的ΔGT值基本相同,尤其是反应(a)。在2.2部分的讨论中曾提到,使用物质吉布斯自由能函数法计算包含Ba(OH)2

Table 3. Standard formation molar Gibbs free energy ΔGf,T in reference [11] , the unit is kJ∙mol−1

表3. 相关物质的生成标准摩尔吉布斯自由能 [11] ∆Gf,T,单位为kJ∙mol−1

Table 4. Gibbs free energy change ΔGT of the reactions in Table 1 calculated using Gibbs free energy function method, the unit is kJ∙mol−1

表4. 使用物质吉布斯自由能函数法,表1中的化学反应在不同温度下的吉布斯自由能变ΔGT,单位是kJ∙mol−1

Table 5. Gibbs free energy change ΔGT of the reactions in Table 1 calculated using standard formation molar Gibbs free en ergy method, the unit is kJ mol−1

表5. 使用物质生成标准摩尔吉布斯自由能法,表1中的化学反应在不同温度下的吉布斯自由能变ΔGT,单位为kJ∙mol−1

Figure 1. Gibbs free energy change ΔGT values of the reactions (a)-(f) in Table 1, calculated using Gibbs free energy function method and standard formation molar Gibbs free energy method, which were labeled as 1 and 2 respectively

图1. 使用物质吉布斯自由能函数法(标记为1)和使用物质生成标准摩尔吉布斯自由能法(标记为2)计算,化学反应(a)-(f)在不同温度下的吉布斯自由能变ΔGT

的反应(本研究中反应(e)和(f))会造成计算结果与真实情况的偏差。然而,用两种方法对反应(e)和(f)的计算结果是相似的,如图1所示。

除了反应(c)之外,ΔGT的值均为正数,表明这些反应在标准状态下很难向正向进行。对于反应(c),通过两种方法计算发现ΔGT随着T的升高而升高,700 K时的ΔGT仍为负值,但在更高的900K和1000K时,T为正值。

3.2. 氟化钡与碳酸钡的转化反应

700 K (约427℃)时,ΔGT值为负是导致在低温淬火处理低氟含量前驱溶液制备的实验样品中有BaCO3存在的原因。在我们之前的研究中 [6] ,发现使用氟含量为传统TFA-MOD法10.3%的低氟溶液时,利用衰减全反射傅立叶变换红外光谱可以在400℃检测到BaCO3的存在。在金利华等人的研究中 [12] ,使用氟含量为7.7%的前驱溶液,X射线衍射测量也可在400℃和500℃检测到BaCO3相存在。

此外,在上述两项研究中 [6] [12] ,在较高的温度下没有检测到BaCO3。这种现象可能归因于两个方面。首先,反应(c)的ΔGT随T升高而升高,在更高的温度下变为正值,导致反应(c)向相反方向进行,使BaCO3转化为BaF2。其次,在MOD热处理中炉管中一直通入含氧气流 [6] ,会使二氧化碳不断从薄膜中排除出去,这也会导致BaCO3向BaF2转化的反应进行。

4. 结论

在本研究中,使用吉布斯自由能函数法和标准摩尔生成吉布斯自由能法两种方法,计算温度范围为700 K到1000 K的吉布斯自由能变化ΔGT,来分析BaF2可能的转化反应。采用两种方法计算的ΔGT值整体是相似的。研究发现BaF2转化为BaCO3的反应的ΔGT在700 K为负数,而在更高温下为正数,这与低氟前驱溶液的MOD-YBCO研究一致。本研究可以在较高的温度下验证BaF2的相稳定性并有助于探讨MOD-YBCO工艺热处理的中间相的演变过程。

文章引用

卢弘愿,冯 峰,吴 蔚,张向松,汪林立,瞿体明,翟胜军,冯平法. 钇钡铜氧超导膜溶液法沉积过程中氟化钡中间相的热力学分析
Thermodynamics Analysis on BaF2 Intermediate Phase in Solution-Derived YBCO Superconducting Film Deposition[J]. 材料科学, 2017, 07(02): 232-237. http://dx.doi.org/10.12677/MS.2017.72030

参考文献 (References)

  1. 1. Holesinger, T.G., Civale, L., Maiorov, B., et al. (2008) Progress in Nanoengineered Microstructures for Tunable High-Current, High-Temperature Superconducting Wires. Advanced Materials, 20, 391-407. https://doi.org/10.1002/adma.200700919

  2. 2. Hu, R., Dong, H., Li, J., et al. (2008) Study on Microstructure Characterization of YBCO Bulk Prepared by Directional Seeded Infiltration-Growth. Rare Metal Materials & Engi-neering, 37, 854-858. https://doi.org/10.1016/S1875-5372(09)60022-9

  3. 3. Jin, L.H., Lu, Y.F., Feng. J.Q., et al. (2013) Development of Modified TFA-MOD Approach for GdBa2Cu3Oy Film Growth. Materials Letters, 94, 23-26. https://doi.org/10.1016/j.matlet.2012.12.022

  4. 4. Zhao, X., Gao, C., Xia, Y., et al. (2011) Preparation of YBCO Coated Con-Ductors on RABiTS Substrate with Advanced TFA-MOD Method. Rare Metal Materials & Engineering, 40, 342-345.

  5. 5. Huang, R., Feng, F., Wu, W., et al. (2013) A Water-Free Metal Organic Depo-Sition Method for Yba2Cu3O7−δ Thin Film Fabrication. Superconductor Science & Technology, 26, 115010-115016. https://doi.org/10.1088/0953-2048/26/11/115010

  6. 6. Wu, W., Feng, F., Zhao, Y., et al. (2014) A Low-Fluorine Solution with a 2:1 F/Ba Mole Ratio for the Fabrication of YBCO Films. Superconductor Science & Technology, 27, 105-112. https://doi.org/10.1088/0953-2048/27/5/055006

  7. 7. Li, M., Yang, W., Shu, G., et al. (2015) Con-trolled-Growth of Yba2Cu3O7−δ Film Using Modified Low-Fluorine Chemical Solution Deposition. IEEE Transactions on Applied Superconductivity, 25, 1-4.

  8. 8. Goyal, A. (2005) Second-Generation HTS Conductors. Kluwer Academic Publishers, Boston, 179-194. https://doi.org/10.1007/b106635

  9. 9. 叶大伦. 实用无机物热力学数据手册[M]. 第2版. 北京: 冶金工业出版社, 2002: 1-1209.

  10. 10. Klotz, I.M. and Rosenberg, R.M. (2008) Chemical Thermodynamic: Basic Concepts and Methods. 7th Edition, Wiley, Hoboken, 1-110. https://doi.org/10.1002/9780470285237.ch1

  11. 11. Barin, I. (1995) Thermochemical Data of Pure Substances. 3rd Edition, WILEY-VCH Verlag GmbH, Weinheim 1-1885. https://doi.org/10.1002/9783527619825

  12. 12. Jin, L.H., Li, C.S., Feng, J.Q., et al. (2016) Optimization of Fluorine Content in TFA-MOD Precursor Solutions for YBCO Film Growth. Superconductor Science & Technology, 29, Article ID: 015001. https://doi.org/10.1088/0953-2048/29/1/015001

  13. NOTES