Preparation and Properties of Hydrophobic Alginate Based Aerogels

Maowen Tang1,2, Bin Hui2,3, Miao Yang1,2, Yougang Gui1,2, Wenliang Zhang1,2, Bingbing Wang2,3*

1College of Materials Science and Engineering, Qingdao University, Qingdao Shandong

2Institute of Marine Biobased Materials, Qingdao University, Qingdao Shandong

3State Key Laboratory of Bio-Fibers and Eco-Textiles, Qingdao University, Qingdao Shandong

Received: Mar. 3rd, 2019; accepted: Mar. 18th, 2019; published: Mar. 26th, 2019

ABSTRACT

Natural polysaccharide-based aerogel materials have attracted much attention due to their excellent properties. However, it contains hydrophilic groups such as hydroxyl groups and carboxyl groups, which greatly limits its application in specific aspects. In this paper, sodium alginate-based aerogels were prepared by sodium alginate as raw material and treated with ethanol. A hydrophobic alginate-based aerogel was prepared in a solvent xylene using octadecyltrichlorosilane as a hydrophobic modifier. The hydrophobic alginate-based aerogel has a rough surface, a striped region appears in the surface microstructure, and Si element and C=O bond appear, indicating that the modification is successful. After hydrophobic modification, the adsorption rate of oils is improved and more selective.

Keywords:Sodium Alginate, Aerogel, Hydrophobic

疏水型海藻酸钠基气凝胶的制备及性能研究

唐茂文1,2,惠彬2,3,杨苗1,2,桂由刚1,2,张文良1,2,王兵兵2,3*

1青岛大学,材料科学与工程学院,山东 青岛

2青岛大学,海洋纤维新材料研究院,山东 青岛

3青岛大学,生物多糖纤维成形与生态纺织国家重点实验室,山东 青岛

收稿日期:2019年3月3日;录用日期:2019年3月18日;发布日期:2019年3月26日

摘 要

天然多糖基气凝胶材料因其优异的性能备受关注。但自身含有羟基、羧基等亲水基团,极大地限制了其在选择性吸油方面的应用。本文以海藻酸钠为原料,经过乙醇处理制备了海藻酸钠基气凝胶。以十八烷基三氯硅烷为疏水改性剂,在溶剂二甲苯中制备了疏水型海藻酸钠基气凝胶。疏水型海藻酸钠基气凝胶的表面粗糙,表面微观结构中出现条纹状区域且出现了Si元素和C=O键,表明改性成功。经过疏水改性后对油类的吸附率得到提升并且更加具有选择性。

关键词 :海藻酸钠,气凝胶,疏水

Copyright © 2019 by authors and Hans Publishers Inc.

This work is licensed under the Creative Commons Attribution International License (CC BY).

http://creativecommons.org/licenses/by/4.0/

1. 引言

当今社会,环境污染严重,在水资源中常见垃圾、重金属离子、浮油等污染物 [1] 。对于水中浮油的收集是一项重要工作。目前常利用吸附浮油,对浮油进行原位燃烧和分散降解等三种方式处理浮油。吸附法由于简便快捷,不需要大量的设备,只需要对局部污染处使用吸附剂即可去除浮油,在紧急处理泄露原油方面具备很大的优势 [2] 。常用的锯末等吸附材料在吸附原油的同时也会吸附大量的水,效率极低且不易回收 [3] 。一些高分子类的合成吸附剂在吸附的同时也会造成自身质量的损失 [4] 。

海藻酸钠是一种从海带、褐藻等藻类中提取的天然多糖类物质 [5] ,原料来源广泛且生物可降解 [6] ,是一种极好的环保材料。利用海藻酸钠制备成海藻酸钠基气凝胶可作为吸附材料使用 [7] 。海藻酸钠基气凝胶表面带有大量的羟基、羧基等亲水基团,较好的亲水性限制了其在吸油领域的应用。近年来很多报道指出通过表面烷基化或者酯化等改性反应可以对天然多糖基气凝胶进行疏水改性,得到疏水型天然多糖基气凝胶 [8] [9] 。

本实验以海藻酸钠为原料制备气凝胶,以十八烷基三氯硅烷为改性剂,通过表面酯化改性反应制备了一种疏水性良好、结构稳定且环境友好型的疏水型海藻酸钠基气凝胶。对其表面形貌、结构、元素组成及分布、静态接触角等进行了分析表征,并对吸油率做了简单测试。

2. 实验部分

2.1. 主要原料与仪器

海藻酸钠(Sodium alginate):山东洁晶集团股份有限公司;十八烷基三氯硅烷(OTS):上海麦克林生化科技有限公司;二甲苯(Dimethyl benzene):国药集团化学试剂有限公司;无水乙醇(Ethanol):国药集团化学试剂有限公司。

电子天平(ME104E):北京欧信胜科技有限公司;真空干燥箱(DZF-6050):上海圣科仪器有限公司;X射线衍射仪(DX2700):丹东浩元仪器有限公司;傅里叶红外光谱仪(Nicolet is50),赛默飞世尔科技有限公司;X射线光电子能谱仪(Escalab 250):赛默飞世尔科技有限公司;高分辨扫描电子显微镜(Quanta250FEG):美国FEI公司捷克工厂;光学接触角及3D形貌测量系统(Theta):瑞典Biolin公司。

2.2. 海藻酸钠基气凝胶的制备

在室温下,称取16.00 g白色海藻酸钠粉末,在机械搅拌下加入到800 ml去离子水中,配置成2wt%的海藻酸钠水溶液。将配置好的海藻酸钠水溶液脱泡后,倒入缓慢搅拌的乙醇溶液中,会出现白色析出物,浸泡1 h后过滤,得到的凝胶物质是海藻酸钠、去离子水和乙醇的混合物。放入冰箱(−68℃)冷冻48 h。最后将其放入冷冻干燥机中干燥48 h得到经过乙醇处理的海藻酸钠基气凝胶(ESA)。

2.3. 疏水型海藻酸钠基气凝胶的制备

量取50 mL二甲苯溶液,在避光条件下加入1.5 mL十八烷基三氯硅烷(OTS),形成3v/v%的OTS/二甲苯溶液。将ESA浸泡在3v/v%的OTS/二甲苯溶液中1.5 h,然后用二甲苯溶液浸泡洗涤2~3次除去多余的改性剂和副产物。将样品取出放置在通风处12 h使气凝胶中的溶剂慢慢挥发出来,放入真空干燥箱中50℃干燥12 h,得到疏水型海藻酸钠基气凝胶(S-ESA)。

2.4. 疏水型海藻酸钠基气凝胶的吸油率测定

为了测试疏水型海藻酸钠基气凝胶的吸油性能。分别对花生油、真空泵油、二甲基硅油进行了吸附率测定。首先称量原始气凝胶的质量,记作m0,室温下将气凝胶样品浸入到20 ml各种油类中,经过10 min浸泡后取出,用滤纸擦去表面未被吸附的油类,称量其质量记作m1,将该过程重复3次,取平均值。按如下公式计算吸油率:

( g / g ) = ( m 1 m 0 ) / m 0

3. 结果与讨论

3.1. 疏水改性前后海藻酸钠基气凝胶的宏观与微观形貌分析

疏水改性前后海藻酸钠基气凝胶的宏观照片如图1所示。ESA表面看上去比较光滑,褶皱较少,而S-ESA表面失去了光泽,表面比较粗糙,褶皱增多。猜测是在疏水改性过程中溶剂的挥发会产生微弱的毛细管收缩作用,但是仍保持了原有的结构未被破坏。图2即为海藻酸钠基气凝胶(ESA)和疏水型海藻酸钠基气凝胶(S-ESA)的微观形貌。可以看出ESA的表面较为平坦和均匀,局部有轻微的褶皱,无明显的附着物和凸起,而S-ESA由于表面加入了OTS发生了疏水改性反应,使得表面变得比较粗糙,且多处出现条纹状区域。

Figure 1. Macro photo of sodium alginate-based aerogel (a) and hydrophobic alginate-based aerogel (b)

图1. 海藻酸钠基气凝胶(a)和疏水型海藻酸钠基气凝胶(b)的宏观照片

Figure 2. Microscopic morphology of sodium alginate-based aerogel (a) and hydrophobic alginate-based aerogel (b)

图2. 海藻酸钠基气凝胶(a)和疏水型海藻酸钠基气凝胶(b)的微观形貌

3.2. 疏水改性前后海藻酸钠气凝胶的红外光谱分析

图3为疏水改性前后海藻酸钠基气凝胶的红外光谱图。从中可以看出S-ESA在2916−1和2848 cm−1处为C-H键的对称和不对称伸缩振动峰,在1468 cm−1处为−CH3的反对称变形振动和−CH2的对称变形振动,在719 cm−1处为-(CH2)n-的面内摇摆振动,都是由于低表面能的OTS的加入。在1734 cm−1出现了C=O的伸缩振动峰,推测是由于与海藻酸钠基气凝胶的表面或者内部上面的羧基与Si-OH发生了酯化反应形成了新的C=O。

Figure 3. FT-IR diagram of sodium alginate-based aerogel and hydrophobic sodium alginate-based aerogel

图3. 海藻酸钠基气凝胶和疏水型海藻酸钠基气凝胶的FT-IR图

3.3. 疏水改性前后海藻酸钠基气凝胶的元素分析

图4b~图4d和图4f~图4h中可以看出C、O、Na三种元素在其表面的分布,疏水改性前后的样品中三种元素的分布都比较均匀且密集。从图5e的EDS能谱发现S-ESA中出现了Si元素,是由于OTS的加入引入了Si元素且从图4e中也可以看出Si元素在S-ESA的表面分布较为均匀。对疏水改性后的样品进行了表面XPS测试,通过XPS全谱扫描(图5a)可以看出样品表面出现了Si元素,这与EDS能谱的结果是一致的。在C1s高分辨谱图(图5b)中可以看出在284.9 eV、286.7 eV、288.5 eV处出现了三个峰,分别对应C-(C,H)、C-O、C=O三种类型的碳键。而Si2p的高分辨谱图(图5c)中在102.2 eV和103.0 eV处的两个峰分别对应R-SiO和C-SiO2,说明OTS中的Si-Cl发生水解反应生成了Si-OH,随后与羧基发生酯

Figure 4. Surface morphology of alginate-based aerogel (a) and EDS mapping photos (b, c, d) corresponding to the three elements corresponding to C, O, and Na, hydrophobic seaweed The surface topography (e) of the EDS mapping of the Si element in the sodium-based aerogel and the EDS mapping photographs (f, g, h) corresponding to the three elements of C, O and Na

图4. 海藻酸钠基气凝胶的表面形貌(a)和其中的C、O、Na三种元素所对应的三种元素所对应的EDS mapping照片(b、c、d),疏水型海藻酸钠基气凝胶中Si元素的EDS mapping照片覆盖的表面形貌(e)和其中的C、O、Na三种元素所对应的EDS mapping照片(f, g, h)

Figure 5. XPS full spectrum (a) and C1s (b), Si2p (c) high resolution spectrum of hydrophobic alginate-based aerogel, sodium alginate-based aerogel (d) and hydrophobic sodium alginate EDS spectrum of aerogel (e)

图5. 疏水型海藻酸钠基气凝胶的XPS全谱(a)和C1s (b)、Si2p (c)高分辨谱图,海藻酸钠基气凝胶(d)和疏水型海藻酸钠基气凝胶(e)的EDS能谱

化反应生成C-O-Si键,同时出现C=O,这也与疏水型海藻酸钠基气凝胶的红外光谱中出现的C=O峰相对应。而相邻的两个残留Si-OH结合形成Si-O-Si键。

3.4. 疏水改性前后海藻酸钠基气凝胶的静态接触角和表面自由能分析

图6中可以看出ESA和S-ESA的静态接触角差异。ESA表现出一般的亲水性,静态接触角约为44˚。经过疏水改性处理的S-ESA虽然还没有达到超疏水的效果,但是也表现出较强的疏水性,静态接触角约为134.5˚。又利用静态接触角计算出表面自由能的数值。从表1中可以看出加入了OTS这种低表面能的物质使其在ESA的表面发生了酯化反应,降低了ESA表面的表面能,从改性前的58.956变成了改性后的9.623。表面自由能的降低更加证明了ESA从亲水型向疏水型转变。

Table 1. Surface free energy of sodium alginate-based aerogeland hydrophobic alginate-based aerogels

表1. 海藻酸钠基气凝胶和疏水型海藻酸钠基气凝胶的表面自由能

Figure 6. Static contact angle of sodium alginate-based aerogel (a) and hydrophobic alginate-based aerogel (b)

图6. 海藻酸钠基气凝胶(a)和疏水型海藻酸钠基气凝胶(b)的静态接触角

3.5. 疏水型海藻酸钠基气凝胶对不同油类的吸附测试

对两种样品的吸油率进行了简单测试。如图7所示,ESA和S-ESA对花生油、二甲基硅油和真空泵油均具有一定的吸附效果。其中对二甲基硅油的吸附效果较差,而对真空泵油的吸附效果较好,猜测是因为各物质表面基团不同导致结合力不同。进行疏水改性后的S-ESA的吸附效果较ESA的吸油效果具有小幅提升,但更加具有选择性,当在油水混合溶剂中,会有选择的对油类进行吸附。

Figure 7. Adsorption rates of hydrophobic sodium alginate-based aerogels for different oils

图7. 海藻酸钠基气凝胶和疏水型海藻酸钠基气凝胶对不同油类的吸附率

4. 结论

以海藻酸钠基气凝胶作为基底,十八烷基三氯硅烷为改性剂,对海藻酸钠基气凝胶进行疏水改性。通过SEM、FT-IR、XPS和EDS对其进行了表征。结果表明,疏水型海藻酸钠基气凝胶表面较为粗糙,出现条纹状区域。改性过程中发生了酯化反应,在红外谱图上出现了新的C=O的特征峰。XPS和EDS能谱表明直链烷基引入了少量的Si元素,主要以Si-O-C和Si-O-Si的形式存在。EDS mapping图表明各元素在两种物质中分布都较为均匀。对两种样品进行了静态接触角测试和表面自由能的分析。结果表明,改性后的S-ESA具有较为明显的疏水效果,静态接触角可达到134.5˚,表面自由能也大幅度降低,约为9.623。对花生油、真空泵油和二甲基硅油等具有一定的吸附性和较好的选择性,有望在吸油领域得到一定的应用。

文章引用

唐茂文,惠 彬,杨 苗,桂由刚,张文良,王兵兵. 疏水型海藻酸钠基气凝胶的制备及性能研究
Preparation and Properties of Hydrophobic Alginate Based Aerogels[J]. 材料科学, 2019, 09(03): 249-256. https://doi.org/10.12677/MS.2019.93033

参考文献

  1. 1. Aji, M.P., Wiguna, P.A., Karunawan, J., Wati, A.L. and Sulhadi (2017) Removal of Heavy Metal Nickel-Ions from Wastewaters Using Carbon Nanodots from Frying Oil. Procedia Engineering, 170, 36-40. https://doi.org/10.1016/j.proeng.2017.03.007

  2. 2. Banerjee, S.S., Joshi, M.V. and Jayaram, R.V. (2006) Treatment of Oil Spill by Sorption Technique Using Fatty Acid Grafted Sawdust. Chemosphere, 64, 1030-1031. https://doi.org/10.1016/j.chemosphere.2006.01.065

  3. 3. Tiwari, S., Gupta. V.K., Pandey, P.C., et al. (2016) Ad-sorption Chemistry of Oil-in-Water Emulsion from Spent Oil Based Cutting Fluids Using Sawdust of Mangifera indica. Journal of International Environmental Application & Science, 4, 99-107.

  4. 4. Cai, J. and Prausnitz, J.M. (2003) Density Distribution for a Self-Interacting Polymer Adsorbed at An Oil-Water Interface. Journal of Chemical Physics, 118, 9802-9808. https://doi.org/10.1063/1.1569904

  5. 5. Oberyukhtina, I.A., Bogolitsyn, K.G. and Popova, N.P. (2001) Physicochemical Properties of Solutions of Sodium Alginate Extracted from Brown Algae Laminaria Digitata. Russian Journal of Applied Chemistry, 74, 1645-1649. https://doi.org/10.1023/A:1014892816072

  6. 6. Alipour, S., Montaseri, H. and Tafaghodi, M. (2010) Preparation and Characterization of Biodegradable Paclitaxel Loaded Alginate Microparticles for Pulmonary Delivery. Colloids and Surfaces B: Biointerfaces, 81, 521-529. https://doi.org/10.1016/j.colsurfb.2010.07.050

  7. 7. Mallepally, R.R., Bernard, I., Marin, M.A., Ward, K.R. and McHugh, M.A. (2013) Superabsorbent Alginate Aerogels. Journal of Supercritical Fluids, 79, 202-208. https://doi.org/10.1016/j.supflu.2012.11.024

  8. 8. Cheng, Y., Lu, L., Zhang, W., Shi, J.J. and Cao, Y. (2012) Re-inforced Low Density Alginate-Based Aerogels: Preparation, Hydrophobic Modification and Characterization. Carbo-hydrate Polymers, 88, 1093-1099. https://doi.org/10.1016/j.carbpol.2012.01.075

  9. 9. Rafieian, F., Hosseini, M., Jonoobi, M. and Yu, Q.L. (2018) Development of Hydrophobic Nanocellulose-Based Aerogel via Chemical Vapor Deposition for Oil Separation for Water Treatment. Cellulose, 25, 4695-4710. https://doi.org/10.1007/s10570-018-1867-3

NOTES

*通讯作者

期刊菜单