选用二甲基乙酰胺(DMF)溶剂,将聚醚砜(PES)溶解,再与研磨处理的氯化钠(NaCl)致孔剂颗粒混合均匀,采用浇铸法制成PES/氯化钠(NaCl)材料。用去离子水抽提氯化钠形成PES多孔材料,研究PES的孔结构、孔隙率和吸水率等与成孔剂的关系。使用同一粒径致孔剂,得到的PES孔材料的吸水率随着致孔剂用量增大而增大,但是当PES与致孔剂超过一定质量比后,吸水率减小。使用三个不同粒径的致孔剂,PES孔材料的吸水率与孔结构尺寸没有线性关系。采用光学显微镜和扫描电镜对PES孔结构进行了表征,发现该材料是具有孔隙间连通的三维多孔材料。 Dimethylacetamide (DMF) was used as the solvent to dissolve the polymer, and then mixed with the treated sodium chloride (NaCl) porogen granules. The polymer/sodium chloride (NaCl) materials were prepared by casting method. The PES porous materials were extracted with deionized water to study the pore structure, porosity and water absorption of PES. Using the same particle size porogen, the water absorption of the PES pore material increases with the amount of porogen, but when the mass ratio of PES and porogen is more than a certain degree, the water absorption decreased. The water absorption of the PES pore material was not linearly related to the size of the pore structure using three porosens of different particle sizes. The PES pore structure was characterized by optical microscopy and scanning electron microscopy. It was found that the material was a three-dimensional porous material with inter-pore connectivity.
倪卓,林佩芳,杨莎,林泽宇
深圳大学化学与环境工程学院,广东 深圳
收稿日期:2017年7月28日;录用日期:2017年8月11日;发布日期:2017年8月18日
选用二甲基乙酰胺(DMF)溶剂,将聚醚砜(PES)溶解,再与研磨处理的氯化钠(NaCl)致孔剂颗粒混合均匀,采用浇铸法制成PES/氯化钠(NaCl)材料。用去离子水抽提氯化钠形成PES多孔材料,研究PES的孔结构、孔隙率和吸水率等与成孔剂的关系。使用同一粒径致孔剂,得到的PES孔材料的吸水率随着致孔剂用量增大而增大,但是当PES与致孔剂超过一定质量比后,吸水率减小。使用三个不同粒径的致孔剂,PES孔材料的吸水率与孔结构尺寸没有线性关系。采用光学显微镜和扫描电镜对PES孔结构进行了表征,发现该材料是具有孔隙间连通的三维多孔材料。
关键词 :聚醚砜,致孔剂,孔材料,孔结构,吸水性能
Copyright © 2017 by authors and Hans Publishers Inc.
This work is licensed under the Creative Commons Attribution International License (CC BY).
http://creativecommons.org/licenses/by/4.0/
聚合物多孔材料在组织工程领域受到了广泛的关注。组织工程所采用的聚合物孔材料,其孔结构影响细胞的培养效率和细胞本身的生物学行为,其生物相容性等决定着移植后能否与机体很好的适应、结合和修复,材料是否具有一定的机械强度等,是聚合物孔材料是否应用于临床的重要因素 [
聚醚砜(PES)是一种性能优良的聚合物膜材料,其玻璃化温度高达225℃,可在180℃条件下长期使用,且具有耐热、耐酸碱、耐辐射、抗氧化、耐腐蚀以及优越的血液相容性等性能 [
本研究以水溶性良好、容易去除、对人体无害的氯化钠(NaCl)为致孔剂,调节致孔剂粒径、数量,通过溶液浇注/颗粒沥析技术,制备孔隙间相互连通、孔隙间的尺寸由致孔剂数量及大小控制,同时适应于组织生长的多孔PES材料,为该材料应用于不同组织工程的研究医疗应用提供了实验数据。
聚醚砜(PES),吉林大学湖南中试化工厂;N,N-二甲基甲酰胺(DMF),纯度大于99.5%,天津永大化学试剂有限公司;氯化钠:含量大于99.5%,天津市鼎盛鑫化工有限公司;电热鼓风干燥箱,上海速苏进仪器公司;KH2200型超声波清洗器,昆山和剑超声仪器有限公司;集热式恒温加热磁力搅拌器,巩义市予华仪器有限责任公司;不同目数标准检验网筛,浙江上虞市华丰五金仪器有限公司。
氯化钠:外观是白色晶体状,密度:2.165 g/cm3,熔点801℃,沸点:1461℃,易溶于水、甘油,微溶于乙醇、液氨。氯化钠是一种常用的致孔剂,此类致孔剂耐高温,不易发生分解产生气体,致孔剂在材料中占有一定的空间,当复合材料成型后通过去离子水抽提可去除致孔剂而形成孔结构。将氯化钠放入100℃烘箱中3 h,待完全烘干后,碾磨,使用不同目数的网筛分样,分别得筛出粒径为90~100 μm、200~300 μm、800~900 μm的氯化钠颗粒,放入干燥箱中保存备用。
以DMF为溶剂,加入聚醚砜,缓慢加热直至聚合物充分溶胀,直至溶解成均一透明溶液,加入致孔剂搅拌使致孔剂均匀地分布在溶液中,铸模。样品全部放进真空干燥箱进行抽真空,时间为20~30 min,温度为40℃,表干后停止抽真空,放入烘箱,以60℃为初始温度,半个小时为一个单位逐渐调节温度升高20℃,直至180℃,达到恒重以完全除去溶剂。控制致孔剂粒径以及聚醚砜/氯化钠的质量比,制备聚醚砜/氯化钠8组材料。其中,以粒径为200~300 μm的氯化钠作为致孔剂,制备各物质的质量比为n (PES):n(NaCl) = 1:X,X = 0.25、0.5、0.75、1、1.25、1.5的6组多孔材料;以粒径分别为90~100 μm、800~900 μm的氯化钠作为致孔剂,制备n(PES):n(NaCl) = 1:0.5的2组多孔材料。将样品浸泡于去离子水中,去除氯化钠,每隔2 h更换一次去离子水,用饱和硝酸银(AgNO3)溶液检测是否将氯化钠完全除去。
将制备好的样品刷去表面的灰尘和细碎颗粒,放入100℃干燥箱中烘干2小时,烘干至恒重并于干燥器中自然冷却至室温,称量试样质量,随后放入蒸馏水中,分别在0.5 h、2 h、6 h、12 h、24 h时再次称取该试样的质量。平行重复实验次数n = 5,最终取平均值
将厚度为1~2 mm多孔聚醚砜薄膜平置于载物台,观察多孔材料的孔结构形态,包括孔径以及孔隙连通情况。
以样品表面或者横截面朝上作为观察面,喷金后采用扫描电子显微镜(Scanning Electron Microscope, Hitachi S-520, Japan)观察制备的聚醚砜材料的孔隙结构。
参照国标GB/T 1447-2005,将实验制成Ⅱ型试样形式,以0.5 mm/min拉伸速率启动拉伸实验,测试多孔聚醚砜材料力学性能 [
其中,δ为拉伸强度,MPa;F为试样在拉伸至断裂中受到的最大力N;b为样宽度mm;d为试样厚度,mm。
吸水率是表示物体在正常大气压下吸水程度的物理量,是物质吸水性的量度,是评价多孔材料化学性质和结构的一个综合指标,它既反映了材料的有效孔隙率的大小,又反映了材料自身的亲疏水性质。一般情况下,材料的有效孔隙率相同时,吸水率应当相等。吸水率高的三维材料,有利于细胞进入材料内部孔隙生长 [
选择致孔剂NaCl颗粒尺寸为200~300 μm,在致孔剂粒径相同的条件下,研究致孔剂数量对PES孔材料吸水率的影响。如表1及图1所示,其中PES1~PES6分别为PES与NaCl (200~300 μm)质量比1:0.25、
组别 | PES1 | PES2 | PES3 | PES4 | PES5 | PES6 |
---|---|---|---|---|---|---|
0.5h | 24.12 ± 1.20 | 36.74 ± 1.19 | 49.7 ± 1.23 | 64.64 ± 1.24 | 59.75 ± 1.21 | 50.72 ± 1.18 |
2h | 27.12 ± 1.30 | 40.16 ± 1.23 | 56.0 ± 1.15 | 73.58 ± 1.27 | 63.26 ± 1.28 | 55.96 ± 1.24 |
6h | 35.82 ± 1.15 | 49.44 ± 1.17 | 64.89 ± 1.27 | 76.95 ± 1.19 | 68.99 ± 1.20 | 60.17 ± 1.25 |
12h | 37.65 ± 1.21 | 52.16 ± 1.31 | 68.94 ± 1.19 | 82.93 ± 1.23 | 71.77 ± 1.16 | 63.74 ± 1.16 |
24h | 39.06 ± 1.17 | 54.47 ± 1.29 | 70.15 ± 1.26 | 85.89 ± 1.17 | 73.23 ± 1.17 | 65.44 ± 1.22 |
表1. PES多孔材料吸水率比较(n = 5)
图1. PES多孔材料吸水率比较
1:0.5、1:0.75、1:1、1:1.25、1:1.5六组多孔材料。随着致孔剂含量的增加,多孔材料吸水率增加,当PES与NaCl质量比为1:1时,多孔材料吸水率达到最大,吸水率为85.89%,之后,随着致孔剂数量的增加,吸水率减小。随着致孔剂含量的增加孔材料中孔数量增大,吸水率增加,但PES孔材料与致孔剂质量比超过1:1后,孔材料中的孔结构几个或者多个连成一片,形成空间较大的孔结构,未截留住水分子,导致吸水率下降。
表2及图2为致孔剂粒径分别在90~100 μm、200~300 μm、800~900 μm之间,PES与致孔剂质量比为n(PES):n(NaCl) = 1:0.5时的三组PES材料吸水率的比较。从总体上看,随着材料在去离子水中浸泡时间越长,多孔PES材料吸水率越高。在同一时间,PES2 (孔径200~300 μm)较PES7 (孔径90~100 μm)及PES8 (孔径900~1000 μm)吸水率高;从PES7和PES8两组材料的吸水率比较可以看出,在测试0.5 h及2 h时PES7吸水率低于PES8,当6 h再测试两种孔径的吸水率时,可以看出PES7吸水率高于PES8;在吸水率测试过程中吸水率增加大小为:PES7 (25%) > PES2 (18%) > PES8 (14%)。致孔剂为90~100 μm的多孔材料孔数量多而孔径小,吸水较慢;致孔剂为900~1000 μm的多孔材料孔径大而数量少,吸水快,但不利于水分在孔材料中保持;致孔剂为200~300 μm比较适中既有利于水分子吸收,又有利于对水分子的保持。
组别 | PES2 | PES7 | PES8 |
---|---|---|---|
0.5 h | 36.74 ± 1.19 | 24.27 ± 1.23 | 32.43 ± 1.21 |
2 h | 40.16 ± 1.23 | 32.52 ± 1.29 | 38.83 ± 1.27 |
6 h | 49.44 ± 1.17 | 42.72 ± 1.17 | 41.19 ± 1.23 |
12 h | 52.16 ± 1.31 | 46.52 ± 1.26 | 43.14 ± 1.17 |
24 h | 54.47 ± 1.29 | 48.99 ± 1.24 | 46.08 ± 1.29 |
表2. 不同粒径PES多孔材料吸水率比较(n = 5)
图2. 不同粒径PES多孔材料吸水率比较
如图3(A)及图3(B)是以氯化钠为致孔剂制备的多孔聚醚砜孔光学显微镜图,聚醚砜与致孔剂质量比为1:1。图3(A)是多孔聚醚砜薄膜光学显微镜图,从图中我们可以清晰的看到以氯化钠为致孔剂时孔结构偏方形,这与氯化钠晶体的形状有较大的关系,图3(B)是较厚的多孔聚醚砜材料光学显微图,从图中可以看出图中有较多明暗不同的孔结构,1表示颜色最深的黑色区域,光线透不过,没有孔结构,2表示颜色略浅的灰色区域,部分光线可以透过,表示有孔结构,同时表示部分孔隙被挡住,3表示颜色最浅的白色区域,光线直接穿过多孔材料,孔结构处于连通状态。图中可以看出黑灰白三种区域相互交替,可以判断该多孔材料制备成功,形成了预期的连通多孔结构。
如图4是多孔聚醚砜样品表面的电镜照片,图4(A)为致孔剂粒径90~100 μm、聚醚砜与致孔剂质量比为1:1的多孔材料整体孔结构,孔分布较为均匀,孔形状多为不规则方形,孔大小集中在200~300 μm之间,对植入体内的多孔生物材料,若孔为连通孔隙,则允许组织长入。至少100 μm的空隙才有可能使新生骨长入,150 μm为理想孔径 [
图3. 多孔聚醚砜光学显微镜图
图4. 多孔聚醚砜材料SEM图
图5(A)~(F)为聚醚砜/致孔剂质量比逐渐增加(致孔剂粒径为200~300 μm)的多孔材料断面图。随着致孔剂含量的增加,多孔材料的孔结构数量增多,在同一面积的截面图中,孔结构更加密集,独立存在的孔结构数量减少,因此孔隙之间的连通性增加,孔结构在多孔材料中的贯穿率增大。另外,多孔材料中不仅存在致孔剂形成的孔结构,还含有许多10~30 μm孔结构,这主要与制备工艺、制备条件有关。在制备工艺过程中,搅拌使材料内部产生气泡从而在样品形成后出现10~30 μm的孔结构,而孔的大小和数量则与转速、样品含固量有关。研究证明材料孔径为5~40 μm时,允许纤维组织长入。说明该多孔材料中微孔结构有利于纤维组织的生长。
图5. 致孔剂数量不同的多孔聚醚砜材料SEM图(致孔剂粒径200~300 μm)
PES/致孔剂质量比为1:1,致孔剂粒径分别为90 μm~100 μm图6(A)、800~900 μm图6(B)多孔材料断面图,见图6。图6(A)中可以看到该多孔材料孔与孔连通率较高,同时也有少数超过100 μm的大孔,图6(B)为致孔剂粒径为800 μm~900 μm的孔结构截面图,孔径呈梯度分布,这可能与致孔剂粒径有关,在制备多孔材料时,粒径较大的致孔剂下沉造成孔的不均匀分布。图6(C)为致孔剂粒径为800 μm~900 μm多孔材料切面底部放大图,从图中可以看出该多孔材料孔与孔连通率高、孔径大。
表3为致孔剂粒径为200~300 μm多孔材料的力学性能。在致孔剂增加的条件下,多孔材料断裂伸长率逐渐减小,拉伸强度逐渐降低,弹性模量值逐渐变小;当PES与致孔剂质量比为1:1时,材料断裂伸长率最低(3%),材料拉伸强度及弹性模量都降低较大。以氯化钠作为致孔剂,NaCl与PES为物理结合。
图6. 致孔剂粒径不同的多孔聚醚砜材料SEM图
PES | PES与制孔剂质量比 | 断裂伸长率/% | 拉伸强度/MPa | 弹性模量/GPa |
---|---|---|---|---|
1 | 1:0 | 40 | 87 | 1.36 |
2 | 1:0.25 | 21 | 43 | 1.07 |
3 | 1:0.5 | 14 | 32 | 0.75 |
4 | 1:0.75 | 7 | 23 | 0.64 |
5 | 1:1 | 3 | 14 | 0.51 |
表3. 多孔型PES材料力学性能
该致孔剂分散在PES中,氯化钠的惰性性质对PES材料的化学结构没有影响,PES多孔材料力学性能与孔结构的形状,大小、数量有关。随着致孔剂在PES中的数量增加,该材料的力学强度下降,可以达到一些承力较低的骨的力学条件,如松质骨、颈骨、腰骨等 [
以氯化钠为致孔剂,采用溶液浇注/颗粒沥析法,在不同PES/NaCl质量比的条件下,制备PES多孔材料。研究PES孔结构、孔隙率和吸水率等与成孔剂的关系。使用同一粒径致孔剂,得到的PES孔材料的吸水率随着致孔剂用量增大而增大,但是当PES与致孔剂超过一定质量比后,吸水率减小。使用三个不同粒径的致孔剂,PES孔材料的吸水率与孔结构尺寸没有线性关系。PES多孔材料是孔隙间连通的三维多孔结构,随着制孔剂含量增加,该材料断裂伸长率、拉伸强度、弹性模量均有所下降。
深圳市科学技术研究与发展基金资助项目(JCYJ20170302141509023)。
倪 卓,林佩芳,杨 莎,林泽宇. 聚醚砜(PES)多孔材料的制备与表征 Preparation and Characterization of Polyethersulfone (PES) Porous Materials[J]. 合成化学研究, 2017, 05(03): 20-28. http://dx.doi.org/10.12677/SSC.2017.53004