为了降低存在于污水中的重金属离子对自然界以及人体的危害,选用铜铁矿材料CuFeO
2作为催化剂光催化降解水溶液中的六价铬。使用水热法,通过改变加入的铜盐与铁盐间摩尔比,获得最佳比例的CuFeO
2 (2H相),并对其微观结构和表面形貌进行了表征。同时制备了Ni
2+浓度为1%~2%的掺杂样品,其中2% Ni-CuFeO
2可在80分钟内完全降解Cr (VI)。
In order to reduce the harm of heavy metal ions in sewage to nature and human body, CuFeO
2 was selected as the catalyst for photocatalytic degradation of hexavalent chromium in aqueous solution. The optimal CuFeO
2 (2H phase) was obtained by changing the molar ratio of copper salt to iron salt by hydrothermal method, and its microstructure and surface morphology were characterized. At the same time, the doped samples with Ni
2+ concentration of 1%~2% were prepared, in which 2% Ni-CufeO
2 could completely degrade Cr (VI) within 80 minutes.
In order to reduce the harm of heavy metal ions in sewage to nature and human body, CuFeO2 was selected as the catalyst for photocatalytic degradation of hexavalent chromium in aqueous solution. The optimal CuFeO2 (2H phase) was obtained by changing the molar ratio of copper salt to iron salt by hydrothermal method, and its microstructure and surface morphology were characterized. At the same time, the doped samples with Ni2+ concentration of 1%~2% were prepared, in which 2% Ni-CufeO2 could completely degrade Cr (VI) within 80 minutes.
石 柳,卢 坤,邓泉荣,张义强. 镍离子掺杂CuFeO2材料的制备以及光催化性能研究Preparation and Photocatalytic Performance of Ni2+-Doped CuFeO2 Materials[J]. 环境保护前沿, 2023, 13(01): 65-70. https://doi.org/10.12677/AEP.2023.131008
参考文献ReferencesDavis, S.J., Wise, W.R., Recchia, S., Spinazzè, A. and Masi, M. (2021) The Evaluation of the Detection of Cr(VI) in Leather. Analytica, 3, 1-13. <br>https://doi.org/10.3390/analytica3010001Zheng, J., Lv, J., Liu, W., Dai, Z., Liao, H., Deng, H. and Lin, Z. (2020) Selective Recovery of Cr from Electroplating Nanosludge via Crystal Modification and Dilute Acid Leaching. Environmental Science: Nano, 7, 1593-1601.
<br>https://doi.org/10.1039/D0EN00196AUkhurebor, K.E., Aigbe, U.O., Onyancha, R.B., Nwankwo, W., Osibote, O.A., Paumo, H.K., Ama, O.M., Adetunji, C.O. and Siloko, I.U. (2021) Effect of Hexavalent Chromium on the Environment and Removal Techniques: A Review. Journal of Environmental Management, 280, Article ID: 111809. <br>https://doi.org/10.1016/j.jenvman.2020.111809Mahiout, S., Kiilunen, M., Vermeire, T., Viegas, S., Woutersen, M. and Santonen, T. (2022) Occupational Exposure to Cr(VI) in Finland in 1980-2016 and Related Lung Cancer Risk Assessment. Regulatory Toxicology and Pharmacology, 136, Article ID: 105276. <br>https://doi.org/10.1016/j.yrtph.2022.105276Mishra, S. and Bharagava, R.N. (2016) Toxic and Genotoxic Effects of Hexavalent Chromium in Environment and Its Bioremediation Strategies. Journal of Environmental Science and Health, Part C, 34, 1-32.
<br>https://doi.org/10.1080/10590501.2015.1096883Chen, H., Mu, L., Cao, J., Mu, J., Klerks, P.L., Luo, Y., Guo, Z. and Xie, L. (2016) Accumulation and Effects of Cr(VI) in Japanese Medaka (Oryzias Latipes) during Chronic Dissolved and Dietary Exposures. Aquatic Toxicology, 176, 208-216. <br>https://doi.org/10.1016/j.aquatox.2016.05.002Lu, S., Hu, J., Gao, Y., Zhao, Y. and Ma, J. (2022) The Re-moval Mechanism of Cr(VI) by Calcium Titanate: Insight into the Role of Surface Reduced Cr(III) in Removal Process. Applied Surface Science, 601, Article ID: 154235.
<br>https://doi.org/10.1016/j.apsusc.2022.154235Sessarego, S., Rodrigues, S.C.G., Xiao, Y., Lu, Q. and Hill, J.M. (2019) Phosphonium-Enhanced Chitosan for Cr(VI) Adsorption in Wastewater Treatment. Carbohydrate Polymers, 211, 249-256.
<br>https://doi.org/10.1016/j.carbpol.2019.02.003Peng, H. and Guo, J. (2020) Removal of Chromium from Wastewater by Membrane Filtration, Chemical Precipitation, Ion Exchange, Adsorption Electrocoagulation, Electro-chemical Reduction, Electrodialysis, Electrodeionization, Photocatalysis and Nanotechnology: A Review. Environmental Chemistry Letters, 18, 2055-2068.
<br>https://doi.org/10.1007/s10311-020-01058-xTablero Crespo, C. (2018) Potentiality of CuFeO2-Delafossite as a Solar Energy Converter. Solar Energy, 163, 162-166. <br>https://doi.org/10.1016/j.solener.2018.01.091Schmachtenberg, N., Silvestri, S., da Silveira Salla, J., Dotto, G.L., Hotza, D., Jahn, S.L. and Foletto, E.L. (2019) Preparation of Delafossite-Type CuFeO2 Powders by Conventional and Microwave-Assisted Hydrothermal Routes for Use as Photo-Fenton Catalysts. Journal of Environmental Chemical Engineering, 7, Article ID: 102954.
<br>https://doi.org/10.1016/j.jece.2019.102954Deng, Z., Fang, X., Wu, S., Dong, W., Shao, J., Wang, S. and Lei, M. (2014) The Morphologies and Optoelectronic Properties of Delafossite CuFeO2 Thin Films Prepared by PEG Assisted Sol-Gel Method. Journal of Sol-Gel Science and Technology, 71, 297-302. <br>https://doi.org/10.1007/s10971-014-3369-6Deng, Z., Fang, X., Wu, S., Wang, S., Dong, W., Shao, J. and Tao, R. (2015) The Effect of Oxygen Partial Pressure on the Properties of CuFeO2 Thin Films Prepared by RF Sput-tering. Vacuum, 115, 1-5.
<br>https://doi.org/10.1016/j.vacuum.2015.01.025Luo, S., Fluri, A., Zhang, S., Liu, X., Döbeli, M., Harrington, G.F., Tu, R., Pergolesi, D., Ishihara, T. and Lippert, T. (2020) Thickness-Dependent Microstructural Properties of Heteroepitaxial (00.1) CuFeO2 Thin Films on (00.1) Sapphire by Pulsed Laser Deposition. Journal of Applied Physics, 127, Article ID: 065301.
<br>https://doi.org/10.1063/1.5140451Jin, Y. and Chumanov, G. (2016) Solution Synthesis of Pure 2H CuFeO2 at Low Temperatures. RSC Advances, 6, 26392-26397. <br>https://doi.org/10.1039/C6RA01901CSoares, O.S.G.P., Pereira, M.F.R., Órfão, J.J.M., Faria, J.L. and Silva, C.G. (2014) Photocatalytic Nitrate Reduction over Pd-Cu/TiO2. Chemical Engineering Journal, 251, 123-130. <br>https://doi.org/10.1016/j.cej.2014.04.030